| 微珠提高玻纤/环氧树脂抗原子氧剥蚀的研究 |
| |
| 引用本文： | 王明珠,赵小虎,沈志刚,麻树林.微珠提高玻纤/环氧树脂抗原子氧剥蚀的研究[J].北京航空航天大学学报,2003,29(12):1064-1067. |
| |
| 作者姓名： | 王明珠 赵小虎 沈志刚 麻树林 |
| |
| 作者单位： | 北京航空航天大学 航空科学与工程学院, 北京 100083 |
| |
| 基金项目： | 国家高技术研究发展计划(863计划);2002AA732157; |
| |
| 摘 要： | 采用一种新的抗原子氧剥蚀技术来提高航天器用玻璃纤维/环氧树脂复合材料抗原子氧剥蚀的性能,即在玻璃纤维/环氧树脂中加入不与原子氧反应的超细空心微珠颗粒制备出能抗原子氧剥蚀的复合材料.通过对空心微珠/玻璃纤维/环氧树脂复合材料的制备和原子氧剥蚀效应地面模拟试验,发现空心微珠的加入可以有效提高玻璃纤维/环氧树脂抗原子氧剥蚀的性能,在60?h的原子氧试验中,加有空心微珠的复合材料的原子氧剥蚀率可以减小到未添加空心微珠材料时的11％.
|
| 关 键 词： | 航天器 环氧树脂 玻璃纤维 空心微珠 抗原子氧剥蚀 |
| 文章编号： | 1001-5965(2003)12-1064-04 |
| 收稿时间： | 2003-06-30 |
| 修稿时间： | 2003年6月30日 |
Experimental investigations of improving AO-resistant characteristics of glass fiber/epoxy resin composite filled with superfine cenospheres |
| |
| Wang Mingzhu,Zhao Xiaohu,Shen Zhigang,Ma Shulin.Experimental investigations of improving AO-resistant characteristics of glass fiber/epoxy resin composite filled with superfine cenospheres[J].Journal of Beijing University of Aeronautics and Astronautics,2003,29(12):1064-1067. |
| |
| Authors: | Wang Mingzhu Zhao Xiaohu Shen Zhigang Ma Shulin |
| |
| Institution: | School of Aeronautics Science and Technology, Beijing University of Aeronautics and Astronautics, Beijing 100083, China |
| |
| Abstract: | A new technology was adopted to improve AO-resistant characteristics of spacecr aft composites. The superfine cenospheres, which were stable in AO environment, were filled in the epoxy matrix in order to produce the AO-resistant glass fibe r/epoxy resin composite. Cenospheres/glass fiber/epoxy resin composites were pre pared and the AO exposure test was conducted in ground-based AO effect s simulation facility. It was found that the filling of cenospheres effectually protected the glass fiber/epoxy resin against AO erosion. After the AO exposure test of 60 h, the erosion yield of the composite with cenosphere fillers can dec rease to 11% of the composite without cenosphere fillers. |
| |
| Keywords: | spacecraft epoxy resins glass fibers cenosphere AO-resistant |