新型Co基合金Co-9Al-(9-x) W-xMo-2Ta-0.02B的显微组织与高低温力学性能

以新型Co基合金Co-9Al-9W-2Ta-0.02B成分为基础,分别添加了原子分数为2％、4％、6％、9％的Mo元素替代W（分别称2Mo、4Mo、6Mo、9Mo合金,W+Mo的原子分数为9％,无Mo添加的称为0Mo合金）,研究了Mo元素对合金相组成、显微组织形貌、维氏硬度和高低温压缩强度的影响.结果表明铸态合金由Co...

Microstructures and Mechanical Properties of Alloys Co-9Al-(9-x)W-xMo-2Ta-0.02B at Room and High Temperatures

Based on the composition of Co-9Al-9W-2Ta-0.02B, 2at%, 4at%, 6at% and 9at% Mo are added to replace W (hereafter referred to as alloys 2Mo,4Mo,6Mo and 9Mo respectively; Mo-free alloy is referred to as alloy 0Mo). The effect of Mo additions on phase constitution, microstructure, HV hardness and room/high-temperature strength is investigated. It is found that the as-cast alloys show a microstructure composed of Co-base solid solution γ phase and intermetallic Co₃(Al, Me) compound γ' phase (where Me stands for W, Mo and Ta). The γ phase is the matrix and the γ' phase is distributed on the grain boundaries of the γ phase. After 1 350 ℃/8 h solution and 800 ℃/100 h aging, a cubic γ' phase with a size of 200-300 nm homogeneously precipitates in the γ matrix for alloys 0Mo, 2Mo and 4Mo, and the as-cast γ' phase disappears. As for alloys 6Mo and 9Mo, the microstructure is significantly changed; however, no cubic γ' precipitates are found in the γ matrix; instead there is a large number of needle-like TCP precipitates, while the as-cast γ' phase Co₃(Al, Me) compound changes to Co₃(Al, Mo) compound. Abnormal yield characteristic is found for all alloys. As the Mo content increases, the room/high-temperature strength of the heat-treated alloys decreases, and the abnormal yield temperature shifts towards lower temperatures.