Cyclic Oxidation Behavior of an EB-PVD CoCrAlY Coating Influenced by Substrate/coating Interdiffusion |
| |
Authors: | LIANG Tianquana b GUO Hongbo a PENG Hui a GONG Shengkai a a |
| |
Institution: | School of Materials Science and Engineering, Beihang University, Beijing 100191, China b School of Materials Science and Engineering, Guangxi University, Nanning 530004, China |
| |
Abstract: | To reveal the influence of substrate/coating interdiffusion on the cyclic oxidation property of a metallic coating, cyclic oxidation behavior of an EB-PVD CoCrAlY coating on directionally solidified Ni-based superalloy DZ125 at 1 050 oC is investigated. The 40 μm thick CoCrAlY coating has a cyclic oxidation life of around 160 h, and the oxidation constant is 1.915× 10.7 mg4·cm.8·s.1. However, severe spallation of the oxides containing Co, Cr, Ni, Ta and Ti occurs with longer cyclic oxidation. The degradation in oxidation resistance for the coating is related to the depletion of Al due to the oxide spallation and interdiffusion. Severe interdiffusion between the coating and underlying substrate occurs at 1 050 oC. The composition of the substrate has an important effect on the thermal cycling lifetime of the coating. The influencing mechanism is discussed. |
| |
Keywords: | CoCrAlY coating cyclic oxidation degradation interdiffusion substrate composition |
本文献已被 CNKI ScienceDirect 等数据库收录! |
| 点击此处可从《中国航空学报》浏览原始摘要信息 |
| 点击此处可从《中国航空学报》下载免费的PDF全文 |
|