Preparation and Characterization of Fe_3O_4/T-ZnOw Composites

Fe3O4/T-ZnOw composites are fabricated by depositing a layer of Fe3O4 film on the surface of tetrapod-shaped ZnO whisker (T-ZnOw) by ferrite plating method. The morphology, structure and magnetic properties of the composites are characterized by scanning electron microscopy (SEM), X-ray diffractometer (XRD) and vibrating-sample magnetometer (VSM), respectively. The effects of temperature and pH value of ferrite plating on the Fe3O4/T-ZnOw composites and the magnetic properties of composites are studied. It is shown that the chemical environment with pH value at 7.5 is most favorable for the ferrite plating processes by analyzing the main peaks intensity of Fe3O4 in the XRD patterns and the average diameters of the Fe3O4 crystalline. The increase of the ferrite plating temperature with pH value around 7.5 benefits the whole encapsulation of T-ZnOw by the Fe3O4 magnetic films. The composites exhibit ferromagnetic properties and show much lower magnetization intensity than bulk samples at the same magnetic field intensity.

Preparation and Characterization of Fe3O4/T-ZnOw Composites

 Fe₃O₄/T-ZnOw composites are fabricated by depositing a layer of Fe₃O₄ film on the surface of tetrapod-shaped ZnO whisker (T-ZnOw) by ferrite plating method. The morphology, structure and magnetic properties of the composites are characterized by scanning electron microscopy (SEM), X-ray diffractometer (XRD) and vibrating-sample magnetometer (VSM), respectively. The effects of temperature and pH value of ferrite plating on the Fe₃O₄/T-ZnOw composites and the magnetic properties of composites are studied. It is shown that the chemical environment with pH value at 7.5 is most favorable for the ferrite plating processes by analyzing the main peaks intensity of Fe₃O₄ in the XRD patterns and the average diameters of the Fe₃O₄ crystalline. The increase of the ferrite plating temperature with pH value around 7.5 benefits the whole encapsulation of T-ZnOw by the Fe₃O₄ magnetic films. The composites exhibit ferromagnetic properties and show much lower magnetization intensity than bulk samples at the same magnetic field intensity.