扩散连接界面缺陷对Ti-6Al-4V合金力学性能的影响

研究了φ4mm与φ2mm的扩散连接界面缺陷对Ti-6Al-4V合金力学性能的影响。当拉伸载荷方向与缺陷平面平行时,材料的强度与塑性与无缺陷材料相当,这是由于此类缺陷对样品受力截面的面积几乎没有影响。含有φ4mm缺陷试样的拉压疲劳寿命展现出很大的分散性,界面缺陷并未成为裂纹萌生的唯一位置。从表面起裂的样品均处于高寿命区域,而绝大部分从缺陷处起裂的样品均落于低寿命区域。有限元分析表明,当缺陷位于中心位置时其引起的应力集中较小,应力分布梯度较小;缺陷位于边缘位置时,应力集中效应增大。     

DD6镍基单晶涡轮转子叶片失效分析

为了排除某航空发动机DD6镍基单晶高温合金涡轮转子叶片在室温振动试验中发生的裂纹故障,对故障叶片进行了外观检查、断口分析、表面检查、解剖检查、化学成分分析、金相检查、应力分布计算及热模拟试验,确定了故障叶片裂纹的性质和产生原因.结果表明:涡轮转子叶片裂纹为高周疲劳裂纹,叶片局部区域存在异常的γ'筏排组织是导致该叶片产生早期疲劳开裂的主要原因,且附近区域腐蚀过重及结构上处于应力集中区,也促进了疲劳裂纹的萌生及扩展.针对这些故障,建议优化叶片结构并对腐蚀检查进行严格监控,防止出现γ’筏排组织及腐蚀过重现象,从而避免此类故障再次发生.     

TC6钛合金超塑性变形

对TC6钛合金在800~900℃温度区间内,分别进行应变速率为0.0001~0.1 s-1的恒应变速率法拉伸实验和最大m值法超塑性拉伸实验,获得拉伸过程应力-应变曲线,并采用金相显微镜对拉伸后断口附近显微组织进行分析。结果表明：TC6合金表现出良好的超塑性性能,随着应变速率或温度的升高,伸长率先增大后减小,恒应变速率拉伸时,在温度850℃、应变速率0.001 s-1条件下伸长率可达到993%;在同一变形温度下最大m值法拉伸能获得比恒应变速率法更好的超塑性,850℃时伸长率达到1353%;TC6合金在超塑性变形过程中发生了明显的动态再结晶,并随着应变速率和温度的升高动态再结晶行为增强。     

热等静压工艺制备的Ti-6Al-4V薄壁筒的切削加工

为了能够提高钛合金薄壁筒的加工效率,利用热等静压工艺制备了两个具有不同结构的Ti-6Al-4V薄壁筒,研究了夹具、填充泥浆和筒结构对Ti-6Al-4V薄壁筒的外圆表面粗糙度和精度的影响。结果显示,Ti-6Al-4V热等静压薄壁筒经过切削加工能够达到精度要求,填充泥浆降低了弹性回弹,提高了薄壁筒外圆精度;筒结构的内圆环和粗大端能够提高刚度,有效降低了外圆表面粗糙度值;夹具尺寸误差对圆度和同轴度影响较大,较大的尺寸误差显著降低了筒的外圆精度。     

SF6分解气的近红外在线检测技术研究

为满足SF6绝缘电气设备故障监测与预警的实际需求,分析了国内分解气检测研究现状.对比近红外与中红外吸收光谱检测技术,提出近红外吸收光谱技术在线检测的技术方案.计算分析待测气体特征谱线的吸收系数、吸收光程和电路信噪比对精度的影响,完成系统参数设计.提出SF6分解气在线检测系统方案,实现对H2S、HF和CO这3种气体测量.数据分析表明,系统检测精度优于5×10-7,表明该系统满足电力行业在线测量的需求.     

Early effects of low dose C ion or X-ray irradiation on human peripheral blood lymphocytes

The aim of this study was to estimate the acute effects of low dose ¹²C⁶⁺ ions or X-ray radiation on human immune function. The human peripheral blood lymphocytes (HPBL) of seven healthy donors were exposed to 0.05 Gy ¹²C⁶⁺ ions or X-ray radiation and cell responses were measured at 24 h after exposure. The cytotoxic activities of HPBL were determined by 3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyl tetrazolium bromide (MTT); the percentages of T and NK cells subsets were detected by flow cytometry; mRNA expression of interleukin (IL)-2, tumor necrosis factor (TNF)-α and interferon (IFN)-γ were examined by real time quantitative RT-PCR (qRT-PCR); and these cytokines protein levels in supernatant of cultured cells were assayed by enzyme-linked immunosorbent assays (ELISA). The results showed that the cytotoxic activity of HPBL, mRNA expression of IL-2, IFN-γ and TNF-α in HPBL and their protein levels in supernatant were significantly increased at 24 h after exposure to 0.05 Gy ¹²C⁶⁺ ions radiation and the effects were stronger than observed for X-ray exposure. However, there was no significant change in the percentage of T and NK cells subsets of HPBL. These results suggested that 0.05 Gy high linear energy transfer (LET) ¹²C⁶⁺ radiation was a more effective approach to host immune enhancement than that of low LET X-ray. We conclude that cytokines production might be used as sensitive indicators of acute response to LDI.     

机械振动全息分析及其若干问题

本文用球面波多重象全息照相分析物体的机械振动,简要地讨论了球面波多重象全息三维振动分析的基本规律,介绍了用计算机控制的显微光密度计确定由测点振动引起的物光波的相位差技术,用几何光学方法推导了曲面测件图象上测点位置的修正公式,提出了提高全息振动条纹分辨率的方法.本文在15cm长度物体上至少可记录105级能分辨的全息振型条纹.     

TC4钛板飞行器蒙皮零件热校形研究

论述了金属板料热校形机理一一主要是高温下应力松驰及材料的高温软化效应．并根据此原理对某飞行器TC4钛板零件进行热校形，其校形结果达到预期效果。     

基于位置信息的HMIPv6快速切换方案

针对RSVP在HMIPv6下域间(inter-handover)切换延时过大,不能满足实时业务的要求。本文提出一种基于位置信息的HMIPv6快速切换方案,即移动节点进行域间切换时,根据移动节点的运动轨迹预测即将去往的接入路由器,从而提前注册及预留资源。     

锻造LF6法兰阳极化后表面深灰色原因分析

锻造LF6材料法兰硫酸阳极化后表面产生深灰色物质,影响产品质量和性能。分析认为这种现象与材料、机械加工和表面腐蚀有关,为此设计了一系列工艺验证试验,探寻深灰色物质产生的原因。试验结果表明,锻造LF6材料自身所含有的金属元素、机械加工和生产周期过长是阳极化封闭后零件表面产生深灰色的主要原因。