镍基耐高温自润滑刷式封严涂层研究

为满足先进航空发动机刷式封严对涂层材料自润滑耐磨性能的要求,采用等离子喷涂技术制备了NiCoCrAlY-Cr_2O_3和NiCoCrAlY-Cr_2O_3-AgMo两种复合涂层;采用扫描电子显微镜、X射线衍射、拉曼光谱和高温摩擦磨损试验等分析测试手段研究了涂层的物相组成、微观结构、力学性能以及摩擦磨损性能。结果表明:研制的两种新型涂层具有较低的孔隙率、较高的显微硬度和结合强度,从20℃到800℃的磨损量都在10~(-5)mm~3·N~(-1)·m~(-1)数量级,显示出优异的耐磨性能;NiCoCrAlY-Cr_2O_3涂层在摩擦系数随着温度的升高而降低,在800℃达到最低值0.3;NiCoCrAlY-Cr_2O_3-AgMo涂层从400~800℃的摩擦系数一直保持在0.23左右。对其摩擦机理的研究表明:400℃时涂层与高温合金GH4145对磨件之间形成连续的含Ag润滑膜,600℃以上时摩擦表面生成的Ag_2MoO_4自润滑相显著降低了涂层的摩擦和磨损。     

C/SiC复合材料在高能HAN发动机上应用研究

针对高能硝酸羟胺(HAN)发动机特点,联合国防科技大学与贵研铂业股份有限公司研发了新型C/SiC复合材料身部,并进行地面试验。试验结果表明,C/SiC复合材料身部结构完好,表面HfO_2基环障涂层较完整,未出现显著开裂、剥落,涂层效果明显,保证了HAN单元发动机工作寿命。本研究为C/SiC身部在HAN单元发动机上工程化应用提供参考。     

局部规则涂层对气冷叶片测温影响的数值研究

为研究微细热电偶测温安装涂层对其测量精度的影响机理,基于气固耦合传热(CHT)方法,建立了接近真实气膜冷却叶片的三维模型,选择SST(shear stress transport) γ -θ湍流模型,对未喷涂氧化铝涂层与在叶片吸力面前缘、压力面前缘、压力面尾缘处喷涂氧化铝涂层后的气冷叶片表面温度进行数值研究。无涂层工况的数值计算结果与实验结果误差控制在5%以下,验证了数值方法的有效性。研究结果表明:涂层对近壁面燃气的流动特性产生显著影响;三种有涂层工况的数值计算结果表明,压力面前缘处比吸力面前缘处温差波幅小,且比压力面尾缘处测温误差降低35.5%;在压力面及吸力面前缘处,最佳测温区域为涂层中部至下端之间的部位,而在压力面尾缘处,最佳测温区域尽量选择靠近涂层上端部位。      

异形构件化学气相沉积SiC涂层的数值模拟

根据化学气相沉积(CVD)工艺制备SiC陶瓷涂层的工艺特点和典型异形构件的结构特点,建立了异形构件表面化学气相沉积SiC涂层的数学模型。利用该模型,对CVD法在典型异形表面制备SiC涂层进行了数值计算和分析。计算结果显示,带有斜面的构件对CVD SiC沉积过程有显著影响,在反应器大小允许的情况下,构件放置时,斜面与水平面的夹角越小越好,并尽可能将构件长的一面与水平面平行,这样有利于沉积的涂层均匀。此外,对于带有台阶的构件来说,正放的构件表面浓度大于倒放的构件,而浓度梯度则小于倒放的构件。因此,在实际应用中,应尽量使台阶部分放在气流的下游。上述研究结果对CVD工艺制备SiC涂层的优化具有一定的指导意义。     

Impermeability of Y3Al5O12 ceramic against molten glassy calcium-magnesium-alumina-silicate

Degradation of thermal barrier coatings (TBCs) caused by calcium-magnesium-alumina-silica (CMAS) glassy penetration is becoming an urgent issue for TBCs industrial applications. In this work, yttrium aluminum garnet (Y₃Al₅O₁₂, YAG) nano-powders were synthesized through a chemical co-precipitation route. The resistance of YAG ceramic to glassy CMAS infiltration at 1250?°C was evaluated. YAG ceramic bulk sintered at 1700?°C for 10?h was comprised of a single garnet-type Y₃Al₅O₁₂ phase. The molten CMAS glass was suppressed on the surface of the YAG ceramic at 1250?°C. A chemical reaction between YAG and the molten CMAS glass did not occur at 1250?°C for 24?h, suggesting that YAG could act as an impermeable material against glassy CMAS deposits in the TBC field.     

BN/SiBCN light-leakage-proof coatings of silica optical fiber for long term sensors at high temperatures

SiBCN and BN/SiBCN light-leakage-proof coatings were prepared on silica optical fibers for sensing applications at high temperatures. Scanning electron microscopy was used to characterize the surface morphology and microstructure of the coated fiber. Mechanical and optical properties of the coated fiber were characterized by Raman, optical and tensile tests. Compared with the original fiber, the tensile strength of SiBCN and BN/SiBCN coated fiber show an increase of about 60% and 90% at room temperature, respectively. In addition, the tensile strength of BN/SiBCN coated silica optical fiber was increased by about 42% at 700 °C. It has been found that the improvement of the strength of BN/SiBCN coated silica optical fiber is related to the healing of defects and residual compressive stress in fibers. From the light transmittance performance of the coated fiber, it was found that BN/SiBCN double coating could be an ideal total reflection solution to protect silica optical fiber from light leakage during high temperature sensing operation.     

高超声速飞行器TPS破损修复涂料

分别采用环氧树脂和呋喃树脂作为基体混合碳化硅粉末与晶须制备了耐高温修复涂料.以氧-乙炔烧蚀试验测试涂料的耐高温烧蚀性能,用扫描电子显微镜分析烧蚀后涂料表面的微观形貌,用X射线衍射、表面能谱分析对涂料烧蚀后成分进行分析表征.结果表明:碳化硅粉末与晶须的质量分数比为8/4的呋喃树脂/碳化硅体系涂料具有良好的耐高温烧蚀性能,...     

电磁波在吸波涂层中的干涉现象

为研究电磁波在吸波涂层中的干涉现象,选取了X型羰基铁粉吸收剂,采用同轴法测试了材料电磁参数,通过多次反射方法求解了X型吸波涂层在厚度为1/4波长时反射系数公式;另外,求解了不同厚度X-1型吸波涂层对频率为9.5 GHz平面电磁波反射系数公式,取公式前6项计算了反射系数Γ_a和反射率R_a。结果表明,多次反射波之间产生了干涉行为,发生了干涉相消现象。Γ_a、R_a分别与传输线方法计算的Γ和R的值非常接近,表明Γ_a和R_a可以近似代表X-1型吸波涂层对9.5 GHz电磁波的反射系数和反射率。当X-1型吸波涂层厚度小于1.9 mm或在3.2~6.6 mm时,第二反射波对第一反射波起到干涉相长作用,降低吸波性能,表明优选的吸波涂层厚度应该介于1.9~3.2 mm。     

嵌入式中温共固化复合材料阻尼结构制作工艺及层间结合性能

嵌入式共固化复合材料阻尼结构层间易脱层问题的解决对这种新型阻尼结构的应用来说至关重要.本文根据中温固化玻璃纤维/环氧树脂复合材料固化工艺参数,提出用正交实验法研究嵌入复合材料层中的粘弹性阻尼薄膜的组分,探索用刷涂工艺在预浸料表面刷涂不同厚度的阻尼薄膜,然后利用固化工艺制作嵌入式共固化复合材料试件,最后通过阻尼层剪切实验,获得阻尼薄膜厚度与层间最大剪切应力的变化曲线.失效界面分析说明刷涂工艺制成的阻尼薄膜与玻璃纤维/环氧树脂预浸料共固化反应后在层间形成互穿网络结构(IPN)和物理融合,这使得嵌入式共固化复合材料具有更好的层间结合性能.     

疏水涂层表面防冰效果的结冰风洞实验研究

采用结冰风洞实验的研究方法,对不同疏水涂层表面的防冰效果进行了研究,建立了综合考虑结冰外形、结冰速率和结冰强度等量化参数的防冰效果评估方法。实验研究表明,硅橡胶的防冰效果并不明显,但添加16烷的硅橡胶却显示出了更好的防冰效果,因此,在高分子涂层中添加小分子材料是一种值得探索的防冰涂层研究方向。疏水涂层只能降低结冰速率,无法完全杜绝材料表面的结冰现象,需要对涂层配方及其防冰机理进行更深入的研究,才能获得更好的防冰效果。研究结果对于防冰理论和技术的发展具有现实的意义。