新型结构粘接材料对航空有机玻璃性能的影响

选用新型结构粘接材料中低温固化环氧结构胶膜J-351和改性丙烯酸酯液体胶胶黏剂SY-50s,表征胶黏剂对有机玻璃的粘接性能以及应力-溶剂银纹性能,并研究胶黏剂对有机玻璃力学性能的影响。结果表明:两种胶黏剂对有机玻璃具有良好的粘接性能,J-351抗应力溶剂银纹性能优于SY-50s;有机玻璃表面施胶后力学性能下降,与定向有机玻璃相比,浇注有机玻璃力学性能下降更为明显。通过对拉伸试样断口形貌分析发现,拉伸试样带有胶黏剂的一侧首先发生破坏。因SY-50s与有机玻璃界面结合紧密,导致带有SY-50s胶黏剂的有机玻璃力学性能下降程度较大;而J-351环氧胶膜与有机玻璃界面清晰,对有机玻璃力学性能影响相对较小。因胶黏剂对有机玻璃性能的影响,导致采用SY-50s胶黏剂粘接的试样边缘连接强度低于J-351胶黏剂粘接的试样,新型结构粘接材料J-351环氧胶膜在有机玻璃粘接中应用性能良好。     

A novel surrogate modeling strategy of the mechanical properties of 3D braided composites

In this paper, a surrogate-based modeling methodology is developed and presented to predict the elastic properties of three dimensional (3D) four-directional braided composites. Using this approach, the prediction process becomes feasible with only a limited number of training points. The surrogate models constructed using Finite Element (FE) method and Diffuse Approximation, reduce the computational time and cost for preparing experimental samples. In the FE model, multiscale method is applied to couple the computations of elastic properties at microscale and mesoscale. Subsequently, a parametric study is performed to analyze the effects of the three design parameters on the elastic properties. Satisfactory results are obtained via the surrogate-based modeling predictions, which are compared with the experimental measurements. Moreover, the predictions obtained from surrogate models concur well with the FE predictions. This study orients a new direction for predicting the mechanical properties based on surrogate models which can effectively reduce the sample preparation cost and computational efforts.     

Mg-Sc-Y三元合金的微观组织和力学性能

稀土元素作为重要的镁合金强化相元素,其多元添加产生的影响并未得到充分研究。在Mg-Sc二元系的基础上将Y作为第三元加入,制备了Mg-5Sc二元合金及Mg-5Sc-0.5Y,Mg-5Sc-1Y,Mg-5Sc-2Y,Mg-5Sc-3Y,Mg-5Sc-3.5Y(质量分数,%)5种三元合金,并通过光学显微镜(OM)、扫描电子显微镜(SEM)、X射线衍射(XRD)及室温拉伸等试验,研究了Y元素的加入对Mg-Sc二元合金微观组织和力学性能的影响。结果表明:Y元素在合金中的主要存在形式为固溶态,富集于晶界处。随着Y元素含量的提升,合金晶粒度显著减小,屈服强度和硬度大幅提升,Mg-5Sc-3.5Y的屈服强度相比Mg-5Sc提升了约50%。该强度的提升主要是由细晶强化和固溶强化引起的。     

阻燃钛合金Ti40的热物理性能及力学性能

作为一种功能性钛合金,Ti40阻燃钛合金的热物理性能数据首次被报道。采用真空自耗电弧熔炼技术制备的Ti40合金铸锭成分均匀,利用热挤压开坯+包套保护锻造方法制备的板坯组织均匀。性能测试结果表明:Ti40合金的室温抗拉强度为950 MPa级,且在500℃下具有良好的热暴露性能、高温蠕变性能和高温持久性能。在室温到600℃范围内,合金的杨氏模量和剪切模量随着温度的升高呈线性下降,泊松比随着温度升高而缓慢增加;线性热膨胀曲线随着温度升高呈抛物线增加,平均线膨胀系数随着温度的升高呈线性增加。     

Effects of process parameters on mechanical properties of abrasive-assisted electroformed nickel

A cathode mandrel with translational and rotational motion, which was supposed to obtain uniform friction effect on surface, was employed in abrasive-assisted electroforming for revolving parts with complex profile. The effects of current density, translational speed and rotational speed on the deposit properties were studied by orthogonal test. The tensile strength, elongation and micro hardness value were measured to find out how the factors affected the properties. The optimized results show that changes of current density affect the tensile strength of nickel layer most, while translational speed has the most remarkable influences on both elonga-tion and micro hardness. The low rotational speed affects the properties least. In this experiment, a smooth nickel layer with tensile strength 581 MPa, elongation 17%and micro hardness 248HV is obtained by the orthogonal test.     

弹片热机械疲劳试验方法研究及设计

针对弹片的热机械疲劳（TMF）试验要求，采用机械设计技术、机电技术、冷却技术、计算机技术和数据采集技术，提出了压力载荷和热载荷的加载方法，建立了2种载荷5个试验件的并联试验控制系统，并设计了弹片热机械疲劳试验器。试验结果表明:该系统能够同时模拟服役环境下弹片的压力载荷和热载荷。利用该试验系统进行了弹片的热机械疲劳试验，试验结果再现了弹片在服役状态下的失效模式。试验系统具有良好的重复度、较高的加载频率和加载精度。压力载荷最大相对误差为2.4%，绝对误差小于0.5N。温度载荷最大相对误差为3.55%，最大绝对误差为3.89℃。      

PIP工艺制备SiC晶须增强SiCf/SiC复合材料的性能

以不同界面层厚度的SiC纤维为增强相,采用先驱体浸渍裂解工艺(PIP)制备SiC_f(PyC)/SiC复合材料,并在复合材料基体中引入SiC晶须,对其性能进行研究。结果表明:热解碳(PyC)界面层厚度约为230 nm时,SiC纤维拔出明显,SiC_f/SiC复合材料拉伸强度、弯曲强度和断裂韧度分别达到192.3 MPa、446.9 MPa和11.4 MPa?m^1/2;在SiC_f/SiC复合材料基体中引入SiC晶须后,晶须的拔出、桥连及裂纹偏转等增韧机制增加了裂纹在基体中传递时的能量消耗,使复合材料的断裂韧度和弯曲强度分别提高了22.9%和9.1%。     

MD-130 胶黏剂固化工艺及空间适用性研究

为满足航天电子产品的工艺实施和空间服役要求,本文详细开展了MD-130胶黏剂的固化工艺及空间适应性研究。结果表明,在150℃等温固化60 min后其拉伸剪切强度达到18 MPa,表明其为优选的固化工艺。高低温环境冲击和低剂量的粒子辐照后胶黏剂固化反应更加充分,其芯片剪切强度提高,而大剂量辐照致使高分子降解现象明显,造成了胶接强度的降低。经环境试验后,MD-130胶黏剂仍具有良好的力学性能,满足设计使用要求。     

热处理对FeCo-2V-0.5Cr软磁合金力学与磁学性能的影响

针对FeCo-2V-0.5Cr软磁合金,研究了真空热处理时间对其微观组织结构、力学与磁学性能的影响规律,发现在800℃下热处理时间为2h左右时,合金的抗拉强度和延伸率达到最佳,同时仍保持良好的软磁性能,抗拉强度、延伸率以及矫顽力分别为867.8MPa、10.4%以及2.0Oe。进一步对该合金进行附加磁场下的真空热处理,重点研究了合金的交流损耗与矫顽力随附加磁场方式包括磁场撤除温度与磁场下保温时间的变化规律,发现适当的磁场热处理对合金相关力学性能影响不大,但由于合金中产生了单轴各向异性而使合金矫顽力进一步降至1.6Oe。     

WC/C复合涂层海水环境的耐蚀性与摩擦性能

采用非平衡磁控溅射技术在304L不锈钢和单晶硅基底上沉积WC/C多层复合涂层,利用扫描电镜、Raman光谱仪、X射线衍射仪等研究WC/C复合涂层的微观结构,采用纳米压痕仪、划痕测试系统测试涂层的力学性能,利用电化学测试系统和摩擦磨损试验机分别研究涂层在人工配置的海水环境的耐蚀性能和摩擦性能。结果表明:WC/C复合涂层内含有较多类石墨sp2键结构,存在WC1-x相并镶嵌在非晶碳基质中。较之于304L不锈钢基底,WC/C复合涂层在海水环境中表现出更好的耐蚀性与更优异的摩擦适应性。