纤维缠绕角度对CFRP-Al混合圆管横向受载性能影响

基于准静态横向弯曲试验对缠绕工艺下制备的CFRP/Al混合圆管进行抗弯性能和吸能特性研究,分析了混合圆管的破坏模式,基于不同纤维缠绕角度的碳纤维复合材料-铝合金混合圆管三点弯曲试验结果,通过有限元仿真方法研究了内层纤维缠绕角度对其横向抗弯与吸能特性的影响。试验结果表明,CFRP-Al混合圆管横向载荷下的失效形式、损伤模式与纯铝管基本保持一致,但受纤维缠绕角度的影响失效形貌略有差异。纤维缠绕角度越小,CFRP-Al混合圆管的抗弯性能和吸能性越好,同时压溃效率(CFE)明显降低。基于验证的有限元模型,研究不同角度纤维缠绕内层对于表层纤维层的应力传递影响,小角度缠绕内层对于管件的轴向拉伸变形抑制增加了管件整体峰值载荷与吸能作用,大角度缠绕内层对于管件环向刚度的提升增加了整体压溃效率。依此分析可为合理设计CFRP-Al混合管提供有效依据。     

Investigation of anode shaping process during co-rotating electrochemical machining of convex structure on inner surface

A novel co-rotating electrochemical machining method is proposed for fabricating convex structures on the inner surface of a revolving part. The electrodes motion and material removal method of co-rotating electrochemical machining are different from traditional electrochemical machining. An equivalent kinematic model is established to analyze the novel electrodes motion,since the anode and cathode rotate in the same direction while the cathode simultaneously feeds along the line of centres. Acc...     

低密度镁锂合金性能强化与精密成形技术

针对轻质高强和近成形复杂结构的技术要求，提出一种基于低密度镁锂合金薄壁筒形件的等温超塑性双向挤压近净成形方法，研究了铸态成形性能、铸态和轧制态在不同温度下的力学性能变化规律。研究结果表明，铸态下延伸率约12%，抗拉强度约145 MPa，轧制态下延伸率变化不大，但抗拉强度提升到180 MPa以上。采用本论文方法镁锂合金的延伸率和抗拉强度显著提高，分别达到21%和216 MPa，表明高温大变形过程中，实现了晶粒细化，大量增强相弥散在晶粒内部，起到性能强化作用，成功实现其性能强化和复杂结构件的精密成形。     

叶根缘板过渡处特征模拟件双轴弯曲振动疲劳试验研究

摘要：针对转子叶片叶根缘板过渡处高应力比弯曲振动疲劳问题，采用转子叶片结构细节刻画方法设计了特征模拟件，实现了对叶根缘板过渡特征的几何刻画和应力分布模拟。基于模态差异化方法，设计了试验夹具及调频质量块。搭建了模拟件双轴弯曲振动试验系统，试验过程中试样处于高频弯曲振动状态下（>1kHz），测得的试样考核点弯曲应变幅稳定，所搭建试验系统实现了轴向拉伸-高频弯曲振动的转子叶片典型双轴载荷施加。试样宏观断裂位置与有限元计算最大应力点一致，对断口进行了宏/微观分析确定了试样断口疲劳源与裂纹扩展特征，证明采用结构细节刻画方法进行试样设计的合理性及所搭建试验加载系统可行性。     

超宽带相控阵天线的发展现状及星载应用展望

面向卫星载荷小型化、集成化和多功能一体化的发展趋势，具有超宽带、高增益和波束灵活特性的天线是目前星载天线领域的研究热点，其可满足通信、干扰、侦察、探测等多种不同应用场景，具有十分迫切的需求。首先对不同形式的超宽带天线单元进行了归纳梳理，根据天线的机电特性和空间环境适应性情况，给出了星载应用选型建议；其次对不同的超宽带波束形成方式进行了阐述，重点分析了不同波束形成方式的优缺点及其在卫星平台上的适用性；总结了超宽带相控阵天线涉及到的关键技术，对主要的技术途径进行了介绍；最后对超宽带相控阵天线的星载应用技术发展提出了建议，可为我国后续开展星载超宽带相控阵天线的技术研究和工程应用提供参考。     

超高强韧稀土镁合金直筒段锻造成形工艺

基于航天型号对超高强韧稀土镁合金构件产品的迫切需求，本文以航天器中的直筒段产品为研究对象，采用近等温锻造挤压成形工艺技术，开展VW84M高强韧稀土镁合金材料的锻造工艺性能研究，分析了直筒段的工艺结构特点，制定了直筒段的锻造成形工艺，通过三维建模、数值模拟技术和成形工艺试验，研究了直筒段的成形过程，分析了坯料的金属流动、温度变化特点，并通过成形工艺试验试制出锻件产品。结果表明，VW84M稀土镁合金在440 ℃的锻造温度时，在合适的挤压速度下具备良好的塑性成形性能，该材料具备实际工程应用能力；数值模拟得到的挤压载荷为64.72 MN，实际挤压载荷为60 MN，相差7.8 %，数值模拟结果与工程试验有较高的结合度；工艺试验得到的直筒锻产品，切、轴向力学性能指标优于预期，抗拉强度不小于340 MPa、屈服强度不小于210 MPa、延伸率不小于6 %的指标值。直筒段产品金属流线分布较为均匀，切向力学性能优于轴向。     

基于线性位移模式的环形谐振子理论研究

环形谐振子理论是谐振陀螺研究领域的重要内容,然而在目前经典环形谐振子理论中,仍 存在很多问题尚未解决,例如:挠度控制方程不能精确求解环形结构的弯曲问题,获得的二阶弯曲 角频率及进动系数理论解不能充分反映出其随尺寸参数(如高度h、曲率半径r 等)变化的影响规 律等。为了克服上述不足,从环形结构理论的基本假设和基本条件出发,基于环形结构的线性位 移模式假设、虚功原理和哈密顿原理,建立新的环形谐振子理论,包括广义本构关系、平衡方程和 边界条件等,获得环形结构静态弯曲问题的解析求解方法和动态问题的理论解。最后,针对典型 的环形结构静、动态问题,通过与其他理论结果进行对比,验证了理论和求解方法的正确性。工作 表明,进动系数不是恒定的,其值会随着结构尺寸的不同在0.4附近很小范围内发生变化。     

Non-isothermal creep age forming of Al-Cu-Li alloy: Experiment and modelling

Non-isothermal Creep Age Forming (CAF), including loading, heating, holding, cooling and springback stages, is an advanced forming technique for manufacturing high performance large integral panels at short production period and low cost. However, the creep deformation and aging precipitation during heating stage is often neglected in experiments and modeling, leading to low forming precision. To achieve shape forming and property tailoring simultaneously, a deep understanding of the non-isothermal creep aging behavior and the establishment of predictive models are urgently required. A new five-stage creep feature of Al-Cu-Li alloy during the non-isothermal creep aging is observed. The microstructural interactions between the dislocations, solute atoms, Guinier Preston zones (GP zones) and T₁ precipitates are found to dominate the five-stage creep aging behavior. The physical-based model considering temperature evolution history is established to describe the five-stage creep feature. The springback and yield strength of non-isothermal creep age formed plates with different thicknesses are predicted and compared by non-isothermal CAF experiments and corresponding simulations. The CAF experiments show that the springback and yield strength of the non-isothermal creep age formed plate are 62.1% and 506 MPa, respectively. Simulation results are in good agreement with experimental results. The proposed model broadens the application of traditional CAF models that mainly focus on isothermal conditions.     

铝锂合金曲面件超低温成形工艺

针对铝锂合金室温成形性差和热成形性能弱化的难题,利用发现的超低温下伸长率与硬化指数同时提高的双增效应,提出铝锂合金曲面件超低温成形新工艺。通过2195铝锂合金板材在不同温度和热处理状态下的超低温变形行为研究,确定发生双增效应的临界温度为低于-140℃,伸长率可提高至40%以上、硬化指数达到0.44;利用建立的超低温成形工艺实验装置,首次试制出直径200 mm的2195铝锂合金球底曲面件,深径比达到0.55、成形极限提高104%;阐明超低温成形试件壁厚分布规律与回弹规律,最大减薄率为10.3%。     

钛合金超塑性成形过程的数值模拟

以TC4合金层板结构的超塑性成形过程为研究对象,采用有限元软件MARC模拟计算了TC4合金宽弦空心夹芯结构的超塑性成形过程。分别分析了应变速率敏感指数、目标应变速率及扩散连接宽度等参数对贴模过程及壁板厚度分布的影响。结果表明:当应变速率敏感指数较大时,夹芯结构会发生沿纵向挤出延伸变形;当目标应变速率为10-3时,材料表现出较佳的超塑性性能;而扩散连接宽度的大小对超塑性成形后板材壁厚分布的均匀性有一定影响。通过控制最大应变速率的方法,提取出了最优化的压力时间曲线。研究结论可为钛合金空心夹芯结构件的超塑性成形提供理论参考。