高温长期时效对一种镍基单晶合金拉伸和持久性能的影响

研究了高温长期时效对一种镍基单晶合金在室温条件下瞬时拉伸强度和在950℃/240MPa条件下持久性能的影响。结果表明:1000℃短期时效100h,合金室温拉伸强度σb与屈服强度σ0.2与时效前相比没有明显变化,时效超过500h后σb和σ0.2开始显著下降,时效超过1000h后,σb和σ0.2随时效时间延长下降幅度减小;短期时效100h和500h样品在950℃/240MPa条件下的持久寿命大幅度降低,延伸率快速上升,时效时间超过1000h后,持久寿命的下降幅度减小,合金的持久寿命与延伸率均趋于稳定。长期时效后γ'相形貌改变及γ/γ'相界面高密度位错网的破坏是时效后合金室温及高温持久性能持续降低的主要原因。     

基于锥形压入的材料力学性能测试方法研究

通过压入测试以获取工程服役结构、小型构件和焊接结构焊缝过渡区的材料单轴本构关系参数,且根据材料本构关系参数来估算材料的压入硬度对于工程设计和安全评估有重要意义.对于幂律材料,本文依据锥形压入试验原理和弹塑性接触有限元分析(EPFEA),揭示了不同锥角的锥形压头其压入能量比与屈服应力之间存在线性关系,提出了基于能量原理预测金属材料本构关系部分关键参数(弹性模量、屈服应力和硬化指数)的CR-EMI (Constitutive Relationship based on Energy Method of Indentation)方法.同时,基于此种线性关系提出了由Hollomon本构关系模型参数预测硬度的H-EMI(Hardness based on Energy Method of Indentation)方法.通过对多种金属材料进行压入试验和有限元分析,验证了CR-EMI方法和H-EMI方法的有效性与精确性.     

固体推进剂使用寿命快速预测探索研究

研究了活化能法快速预测推进剂使用寿命，结果表明，点斜法与常规加速老化方法结果基本一致，两点法（７０℃、５０℃）预测结果最接近。提出用动态法求活化能用于点斜法进行快速寿命预测。     

焊后时效处理对2219铝合金VPTIG接头微区组织和显微硬度的影响

研究了不同温度焊后时效处理对2219铝合金变极性钨极氩弧焊(VPTIG)接头各微区显微组织的影响,采用显微硬度测试和透射电镜观察分析焊接接头各微区析出相的形貌和分布。结果表明,焊后时效处理温度不同,焊接接头各微区显微组织和硬度发生的变化不同。热影响区中的完全回复区对焊后时效最为敏感,低温处理时显微硬度就有明显增长,并在160℃处理时达到最大涨幅;焊缝区变化相对较小,其显微硬度的最高涨幅出现在210℃,且小于前者;热影响区中的过时效区最为稳定,显微硬度的最大增长同样出现在160℃,但涨幅很小。透射电镜观察表明,焊接接头各微区的显微硬度变化主要与时效强化相的析出行为有关。     

Physical characterization of the deep-space debris WT1190F: A testbed for advanced SSA techniques

We report on extensive ${\mathit{BVR}}_c{I}_c$ photometry and low-resolution ($\lambda /\mathrm{\Delta }\lambda ～250$) spectroscopy of the deep-space debris WT1190F, which impacted Earth offshore from Sri Lanka, on 2015 November 13. In spite of its likely artificial origin (as a relic of some past lunar mission), the case offered important points of discussion for its suggestive connection with the envisaged scenario for a (potentially far more dangerous) natural impactor, like an asteroid or a comet.Our observations indicate for WT1190F an absolute magnitude $R_c={32.45}_{\pm 0.31}$, with a flat dependence of reflectance on the phase angle, such as ${\mathit{dR}}_c/d?～{0.007}_{\pm 2}$?mag?deg^?1. The detected short-timescale variability suggests that the body was likely spinning with a period twice the nominal figure of $P_{\mathrm{flash}}={1.4547}_{\pm 0.0005}\mathrm{s}$, as from the observed lightcurve. In the ${\mathit{BVR}}_c{I}_c$ color domain, WT1190F closely resembled the Planck deep-space probe. This match, together with a depressed reflectance around 4000 and 8500 Å may be suggestive of a “grey” (aluminized) surface texture.The spinning pattern remained in place also along the object fiery entry in the atmosphere, a feature that may have partly shielded the body along its fireball phase perhaps leading a large fraction of its mass to survive intact, now lying underwater along a tight ($～1\times 80$?km) strip of sea, at a depth of 1500?m or less.Under the assumption of Lambertian scatter, an inferred size of ${216}_{\pm 30}/\sqrt{\alpha /0.1}$?cm is obtained for WT1190F. By accounting for non-gravitational dynamical perturbations, the Area-to-Mass ratio of the body was in the range $(0.006?\mathit{AMR}?0.011)$?m²?kg^?1.Both these figures resulted compatible with the two prevailing candidates to WT1190F’s identity, namely the Athena II Trans-Lunar Injection Stage of the Lunar Prospector mission, and the ascent stage of the Apollo 10 lunar module, callsign “Snoopy”. Both candidates have been analyzed in some detail here through accurate 3D CAD design mockup modelling and BRDF reflectance rendering to derive the inherent photometric properties to be compared with the observations.     

改性双基推进剂老化燃烧性能实验研究

用Ｘ射线实时荧屏分析系统对人工加速老化的改性双基推进剂的燃烧性能进行试验研究,结果表明,人工加速老化对双基推进剂的燃速影响不大,但对推进剂的装药结构性能有较大影响。试验发现在７０°Ｃ的老化温度下２４天后,推进剂的结构破坏导致异常燃烧现象明显,辅助试验表明,６０°Ｃ９０天可以认为是该种推进剂的安全界限     

Ti—15—3合金时效性能研究

研究了不同炉号的Ｔｉ－１５－３（Ｔｉ－１５Ｖ－３Ｃｒ－３Ｓｎ－３Ａｌ）合金时效温度、时间以及Ａｌ当量与力学性能的关系。在５００～５４０℃范围内拉伸强度与时效温度呈线性关系,平均斜率为－３ＭＰａ／℃。得出了强度与Ａｌ当量的线性方程式,推算出最佳Ａｌ含量为３．１％～３．３％。采用统计方法研究了强度与塑性关系,并研究了冷加工对时效性能的影响。研究的达到１０８０ＭＰａ强度级别的５２０℃／１０ｈ／ＡＣ的时效制度具有满意的力学性能,并应用于制造飞机阻力伞梁。     

湿热环境苯基阻尼硅橡胶加速老化与寿命预测研究

研究了苯基阻尼硅橡胶的湿热老化过程,重点考察了其拉伸性能、阻尼性能和压缩回弹性能。对于拉伸性能,实验研究表明材料拉伸模量和100%定伸应力均随着温度或者湿度的上升而逐渐提高。对于阻尼性能,损耗系数随着温度或者湿度的上升而逐渐下降。对于压缩回弹性能,压缩永久变形随着温度或者湿度的上升而逐渐上升。另外,温度对苯基硅橡胶性能的影响大于湿度。这主要归因于老化过程中同时发生了侧基氧化和水解,进而导致分子链交联和断裂同时发生。相比于分子链断裂,分子链交联占据了主导作用。最后,采用Peck模型预测了不同温湿度环境下苯基硅橡胶的贮存寿命。由于阻尼性能决定了苯基硅橡胶的减振性能,因此将损耗系数作为评价特征参数。结果表明,在25 ℃下,当相对湿度在80%~40%间变动时,苯基硅橡胶的寿命在18~39 a间变化。此研究有助于进一步理解苯基硅橡胶的老化过程,并且提供了不同湿热环境下苯基阻尼硅橡胶寿命预测的方法。     

高超声速一体化飞行器冷流状态气动特性研究

采用数值模拟和风洞实验方法.对高超声速一体化飞行器缩比模型在发动机关闭以及发动机通流状态下的气动特性进行研究.实验中采用彩色纹影系统对缩比模型飞行器的超声速流场进行显示,并通过六分量应力天平测得了全机的升力、阻力和俯仰力矩,数值模拟气动力系数以及流场特征与实验结果吻合较好,同时分析了飞行器保持静稳定状态下的质心选择范围.结果表明进气道开启之后飞行器升力阻力以及抬头力矩显著下降,但此飞行器配平迎角仍较大.该实验结果验证了数值方法的可靠性并为飞行器构型设计提供了参考数据.     

基于频域参量的石英复合材料孔隙超声表征方法研究

孔隙率对复合材料性能有很大影响。针对高孔隙率复合材料超声表征不足问题,本文把超声功率谱特征和非线性特征应用于表征高孔隙石英酚醛复合材料的孔隙率,即在频域上对比研究孔隙对基波幅值的衰减及谐波幅值的滋生的影响。结果表明:二者均能有效表征高孔隙复合材料的孔隙率。基于频域基波分析的超声功率谱特征参量测量容易,随孔隙增加呈递减变化,在孔隙率较低时具有一定优势;基于谐波分析的超声二阶非线性特征参量,随孔隙增加呈递增变化,对高孔隙率表征更具优势。