A theoretical model of semi-elliptic surface crack growth

A theoretical model of semi-elliptic surface crack growth based on the low cycle strain damage accumulation near the crack tip along the cracking direction and the Newman–Raju formula is developed. The crack is regarded as a sharp notch with a small curvature radius and the process zone is assumed to be the size of cyclic plastic zone. The modified Hutchinson, Rice and Rosengren(HRR) formulations are used in the presented study. Assuming that the shape of surface crack front is controlled by two critical points: the deepest point and the surface point.The theoretical model is applied to semi-elliptic surface cracked Al 7075-T6 alloy plate under cyclic loading, and five different initial crack shapes are discussed in present study. Good agreement between experimental and theoretical results is obtained.     

Coupling damage and reliability model of low-cycle fatigue and high energy impact based on the local stress–strain approach

Fatigue induced products generally bear fatigue loads accompanied by impact processes,which reduces their reliable life rapidly. This paper introduces a reliability assessment model based on a local stress–strain approach considering both low-cycle fatigue and high energy impact loads.Two coupling relationships between fatigue and impact are given with effects of an impact process on fatigue damage and effects of fatigue damage on impact performance. The analysis of the former modifies the fatigue parameters and the Manson–Coffin equation for fatigue life based on material theories. On the other hand, the latter proposes the coupling variables and the difference of fracture toughness caused by accumulative fatigue damage. To form an overall reliability model including both fatigue failure and impact failure, a competing risk model is developed. A case study of an actuator cylinder is given to validate this method.     

气孔缺陷对TA15 钛合金氩弧焊接头疲劳性能的影响

对TA15钛合金氩弧焊接接头的组织和疲劳断裂特征进行了分析,对气孔缺陷和疲劳寿命的关系进行了定量表征.结果表明:疲劳裂纹起源于焊缝的亚表面或者内部气孔缺陷,当气孔尺寸较小时,断口会出现“鱼眼”形貌特征;应力水平较低时,气孔尺寸对疲劳寿命的影响尤为显著,在特定的应力水平下,可以通过构件中的气孔缺陷尺寸来预测其寿命,对于焊接结构疲劳寿命的预测和构件焊接质量的评定具有重要的工程意义.     

机载蒸发循环系统结构的稳健性研究

机载蒸发循环系统结构的疲劳寿命易受外界和内部环境的影响,导致无法满足设计要求。采用随机有限元法,参照设计变量和随机变量的变异性,建立机载蒸发循环系统结构疲劳寿命稳健性优化的数学模型;通过引入权因子α,将稳健性优化问题转化为结构疲劳寿命均值和标准差的双目标优化问题。结果表明:合理设置疲劳寿命均值和标准差的权因子,可有效降低设计变量和随机变量对变异的敏感性,进而提高机载蒸发循环系统结构疲劳寿命的稳健性。     

加温超载处理对提高30CrMnSiA钢构件裂纹扩展寿命的作用

对带裂纹的３０ＣｒＭｎＳｉＡ钢紧头等拉伸试件进行同时加温超载处理，经卸载冷却后，在裂纹端区产生残余压应力塑性场。这一处理方法起到延缓裂纹扩展、抑制起裂的效果。     

基于Tanaka-Mura模型的电子束焊接头疲劳裂纹萌生模拟

为揭示高温合金电子束焊接头的疲劳特性,对其开展了疲劳裂纹萌生数值模拟研究。考虑焊缝区微观组织特性,对Voronoi图法进行改进,建立了焊缝区包含柱状晶、细等轴晶及粗等轴晶的混合晶区微观组织模型;对ABAQUS进行二次开发,考虑晶粒随机取向,生成晶粒多滑移带模型。基于Tanaka-Mura位错滑移模型,编写了疲劳裂纹萌生算法,考虑晶界处裂纹的连接与合并,对算法进行了改进,并结合有限元计算建立了电子束焊接头疲劳裂纹萌生数值模拟方法。基于上述方法对GH4169电子束焊接头不同载荷大小的疲劳裂纹萌生进行数值模拟,分析了裂纹萌生过程及萌生寿命,并与试验结果进行对比验证;还探讨了不同热影响区晶粒尺寸对焊接接头疲劳裂纹萌生的影响规律。结果表明,电子束焊接头疲劳裂纹均萌生于热影响区,但随着载荷水平的提高,萌生位置向熔合区一侧靠近;当热影响区晶粒尺寸与母材区晶粒尺寸越接近时,接头疲劳寿命越长。     

化学镀镍层对30CrMo及LY12疲劳性能的影响

研究了两种不同磷含量化学镀镍层的组织结构、硬度及弹性模量,并着重研究了３０ＣｒＭｏ及ＬＹ１２经化学镀镍后的旋转弯曲疲劳性能。结果表明,低磷微晶镀层较高磷非晶镀层具有更高的硬度、弹性模量和疲劳抗力;化学镀镍层导致了３０ＣｒＭｏ疲劳强度的显著下降,但能提高ＬＹ１２的疲劳强度,表明化学镀镍层对基体疲劳性能的影响作用主要取决于基体本身疲劳抗力的高低。     

正交各向异性材料粘塑性损伤统一本构关系研究

用损伤力学与粘塑性理论相结合的方法,将正交个性异性材料的粘塑性统一本构模型［１］进行了修正和推广,建立了在蠕变与疲劳载荷交互作用下正交各向异性材料的粘塑性损伤统一本构模型。用该模型预测了ＤＤ３ 单晶合金的蠕变和疲劳特性以及蠕变和疲劳损伤,预测了在循环载荷作用下材料的蠕变与疲劳交互作用损伤及其寿命。同时将计算结果和试验结果进行了比较     

某Ⅰ级涡轮盘低循环疲劳寿命试验研究

为了确定某Ⅰ级涡轮盘的技术寿命,根据该盘的标准循环载荷谱,对该盘进行了应力分析,确定在标准循环时该盘中心孔与径向销孔相交处为考核部位。为模拟标准循环时该盘在其考核部位的应力谱,专门设计了该Ⅰ级涡轮盘的试验转子及试验参数,在轮盘低循环疲劳试验器上,对该Ⅰ级涡轮盘的一个旧盘进行了高温低循环疲劳试验。试验结果表明：该旧盘低循环疲劳试验至第６０４７ 次循环时,有５ 个销孔考核部位出现了裂纹。断口分析表明：该旧盘剩余的试验低循环疲劳失效寿命为６０４７ 周     

奥氏体合金熔焊接头形变再结晶态的疲劳性能

焊接接头的微观组织和力学性能不均匀性影响疲劳性能,常用焊后热处理等工艺方法来改善。但奥氏体型合金固态无同素异构转变,焊后热处理难以明显地改善其微观组织和疲劳性能。形变再结晶工艺可以同时改善其微观组织和力学性能,进而可以非常显著地提高该焊接接头的抗疲劳断裂能力。本文主要讨论１Ｃｒ１８Ｎｉ９Ｔｉ熔焊接头形变再结晶态的微观组织和疲劳性能,并以该焊接接头的低循环疲劳性能来验证