将复合材料加筋层板受低速冲击后的损伤区域描述为一个椭圆形弹性核,材料在核区的弹性模量下降由冲击表面的凹坑深度确定。利用含任意椭圆核各向异性板杂交应力有限元来模拟含损伤区域,杆单元来模拟筋条,钉单元模拟铆钉（胶层）和常规8节点等参单元模拟其余无损区域,建立起含低速冲击损伤复合材料加筋层板的力学响应分析方法。利用基于特征曲线概念的点应力判据、最大正应力判据和最大剪应力判据分别预测蒙皮的破坏、筋条的破坏和铆钉（胶层）的破坏,从而预测加筋层板在压缩载荷下的剩余强度,获得了与试验相吻合的结果。最后讨论了损伤尺寸、损伤形态、铺层比例等参数对加筋层板剩余强度的影响。     

玻璃纤维增强铝合金层板高速冲击损伤容限

为研究玻璃纤维增强铝合金（GLARE）层板高速冲击损伤容限,对单次、多次冲击载荷下GLARE层板的损伤特性进行了高速冲击试验和数值仿真研究。采用一级气体炮,在GLARE层板靶板的中心位置、边位置、角位置进行弹道冲击试验,获取弹道极限和损伤模式,然后结合数值仿真剖析动态响应特性。结果表明,弹道冲击条件下,GLARE层板主要通过塑性变形、金属层裂纹、脱胶、复合材料纤维脆断等损伤模式吸收冲击能量。边界约束效应对GLARE层板冲击损伤特性具有显著影响,主要表现在：约束效应导致不同位置冲击下GLARE层板损伤模式不同,包括成坑、金属裂纹和冲塞等特征;角位置冲击条件下,GLARE层板的弹道极限速度明显低于中心位置冲击结果;重复冲击条件下,角位置比与边位置和中心位置更容易发生穿透。     

T800/5228A层合板Ⅰ型断裂韧性优化

冷场发射扫描电镜表明,固化5228A/PAEK共混体系发生了反应诱导相分了海岛-双连续-相反转的演化过程;DMA试验表明,PAEK的引入对5228A基体树脂T会改变原有树脂体系的使用温度;T800/5228A经韧化后,在层间内形成了典型的相反转结现出波纹状,明显区别于原有的光滑平直裂纹路径,Ⅰ型层间断裂韧度(GIC)大幅度提高.     

T800/5228A 复合材料层间增韧改性

针对T800/5228A复合材料体系,采用改性聚芳醚酮(PAEK)增韧膜进行层间韧化,设计T800/5228E材料体系。冷场发射扫描电镜显示,T800/5228E层间具有富5228A/富PAEK双连续相结构。张开(Ⅰ)型与剪切(Ⅱ)型韧性试验表明,相比于T800/522A,T800/5228E的GIC与GIIC数值分别提高了68.01%与30.97%,破坏断面显示"钉铆"效应,大量微裂纹以及富PAEK相塑性变形可能主导了上述增韧效果,而张开(Ⅰ)型相比于剪切(Ⅱ)型破坏模式更有利于提供富PAEK组分塑性变形空间则可能是GIC改善效果更佳的缘由。     

含低速冲击损伤层合板的压缩破坏研究

层合板低速冲击后的压缩破坏研究对于复合材料结构设计具有重要意义.按照ASTM D 7136、D 7137试验标准对CCF300/5228层合板进行低速冲击和压缩试验;基于累积损伤理论,以低速冲击数值仿真得到的损伤作为初始损伤,结合应变失效准则和材料性能退化方法,建立含低速冲击损伤层合板的压缩破坏分析模型;使用该模型研究CCF300/5228层合板的损伤演化过程和剩余压缩强度.结果表明：该模型能够较好地解释试验过程中的损伤现象,预测含冲击损伤层合板的剩余压缩强度;损伤扩展和破坏模式与试验结果一致性好.     

T800/5228A 层合板I 型断裂韧性优化

冷场发射扫描电镜表明,固化5228A/ PAEK 共混体系发生了反应诱导相分离,相形貌依次经历
了海岛-双连续-相反转的演化过程; DMA 试验表明,PAEK 的引入对5228A 基体树脂Tg 略有影响,但基本不
会改变原有树脂体系的使用温度;T800/5228A 经韧化后,在层间内形成了典型的相反转结构,裂纹扩展路径呈
现出波纹状,明显区别于原有的光滑平直裂纹路径,玉型层间断裂韧度(GIC)大幅度提高。     

RFI工艺成型两种环氧树脂基复合材料性能比较

采用RFI工艺分别成型了648和5228A环氧树脂基复合材料层合板,其增强材料为碳纤维无屈曲织物,铺层方式为[(0,90)/( 45)]s;测试了两组层舍板的拉伸性能、弯曲性能和层间剪切性能并做了比较分析;对破坏形式和机理进行了探讨.结果表明:5228A相对于648环氧树脂膜有较宽的低黏度区域,较长的凝胶时间;5228A与648层合板相比,拉伸强度高106%,拉伸模量、泊松比接近;弯曲强度高58%,弯曲模量高16%;层间剪切强度高62%.     

碳纤维/双马复合材料层板疲劳损伤累积和寿命估算

给出了T300/QY8911材料单向板和多向层合板在不同应力水平下的拉-拉疲劳试验结果,提出了以疲劳应变累积为基础的损伤累积模型和相应的寿命估算方程。对于以纤维断裂和基体拉伸开裂损伤累积为控制因素的层板,理论结果与试验值十分吻合。     

新型纤维金属混合层板结构的疲劳裂纹扩展与分层行为

为了研究一种新型混合层板的损伤容限性能,针对两种铺层混合层板结构进行了应力比R=0.1,-1下两种锯切缺口尺寸试样的疲劳裂纹扩展试验,对比分析了获得的裂纹扩展a-N曲线数据,并通过对试样进行腐蚀去层,研究了层板的各层分层形态。结果表明,在应力比R=0.1时该新型混合层板疲劳裂纹扩展性能明显优于铝合金板;预浸料两侧添加胶膜比不添加胶膜会导致较好的疲劳裂纹扩展性能;由于裂纹桥接机制作用,锯切缺口尺寸较短层板试样比较长层板试样有较好的裂纹扩展性能;层板中心层铝板较其它层铝板裂纹扩展明显滞后;内层铝板与预浸料间沿裂纹方向呈近似三角形分层。     

低速冲击下FMLs、铝板和复合材料的损伤对比

为提高飞机结构的损伤容限和抗冲击性能,欧洲成功研制了多种纤维金属层板(FMLs),并在具体机型结构上成功应用。对由玻璃纤维和2024-T3铝合金交替层压而成的FMLs进行落锤低速冲击试验,并与2024-T3铝合金板和准各向同性F300复合材料板进行了对比分析。FMLs完全穿透所需要的能量比2024-T3铝合金板和复合材料板分别高出约40%和6倍;在相同能量下,FMLs的背面裂纹长度比铝合金板短30%~50%。使用有限元法对FMLs动态冲击损伤过程进行了数值模拟,其中铝层采用延性损伤理论,纤维层采用Hashin失效准则,分析了层合板的动态冲击响应,总结了其损伤规律。数值结果与试验结果符合较好。     

复合材料层合板鸟撞损伤及吸能影响因素数值分析

数值分析是进行复合材料构件抗鸟撞损伤设计工作中的重要内容.主要采用瞬态非线性有限元分析方法结合文献试验对层合板鸟撞过程进行数值分析,分析了鸟撞层合板的初始损伤情况以及某一时刻各层的应力、应变情况;对比分析了铺层顺序、层合板参数、鸟体参数的变化对层合板吸收能量的影响.分析结果对航空复合材料层合构件抗鸟撞研究具有一定的参考价值.      

混合机织复合材料刚度、强度及低速冲击性能试验研究

将二维机织碳布和单向预浸料碳布按照一定比例铺设成的混合机织复合材料兼具比刚度、比强度高、抗低速冲击损伤以及工艺性好等优点。试验测定不同比例的混合机织复合材料的面内刚度、强度,采用落锤法进行多个能量级别的低速冲击试验和准静态横向压缩试验,用超声波C-扫描法记录各试验件的内部损伤面积,并测量剩余压缩强度,分析这种混合机织复合材料在综合考虑刚度、强度以及低速冲击损伤容限等因素下的最佳铺层比例。     

二维叠层C/SiC复合材料低能量冲击损伤实验

C/SiC复合材料是航空航天器中的耐高温材料,其服役环境存在低能量冲击源且关于此类冲击事件的研究相对较少。本文主要采用落锤冲击系统性地揭示2D叠层C/SiC复合材料平板的抗低速低能量冲击性能,通过改变冲击能量考核不同单层厚度和平板厚度的抗冲击性能变化,并利用CT技术进行冲击后无损检测,分析结构内部细观损伤。结果表明：冲击载荷下,C/SiC复合材料按冲击载荷变化可分为线性、屈服和回弹3个阶段;典型冲击损伤形式包含局部压溃、分层、纤维断裂及基体微裂纹;同等结构厚度,单层厚度越大C/SiC复合材料平板冲击变形和冲击损伤越小,冲击阻抗值越高;同等单层厚度下,结构总厚度较大的C/SiC复合材料平板冲击损伤较小,冲击阻抗较大。因此,C/SiC复合材料的预制体层数与结构厚度对低能量冲击源较为敏感,且减小单层厚度及增加结构总厚度可明显提高其抗冲击性能。     

Static Analysis of Functionally Graded Sandwich Plates Using an Efficient and Simple Refined Theory

In this paper, a new displacement based high-order shear deformation theory is introduced for the static response of function-ally graded sandwich plate. Unlike any other theory, the number of unknown functions involved is only four, as against five in case of other shear deformation theories. The theory presented is variationally consistent, has strong similarity with classical plate theory in many aspects, does not require shear correction factor, and gives rise to transverse shear stress variation such that the transverse shear stresses vary parabolically across the thickness satisfying shear stress free surface conditions. Two common types of functionally graded sandwich plates, namely, the sandwich with functionally graded facesheet and homogeneous core and the sandwich with homogeneous facesheet and functionally graded core, are considered. Governing equations are derived from the principle of virtual displacements. The closed-form solution of a simply supported rectangular plate subjected to sinu-soidal loading has been obtained by using the Navier method. The validity of the present theory is investigated by comparing some of the present results with those of the classical, the first-order and the other higher-order theories. It can be concluded that the proposed theory is accurate and simple in solving the static bending behavior of functionally graded sandwich plates.     

复合材料层合板抗冲击损伤的参数表征

研究了铺层方式为［０２／９０２／４５２／－４５２］ｓ的航空用碳纤维增强树脂基复合材料（ＣＦＲＰ）准各向同性层合板低速冲击引起损伤的表征问题。通过落重冲击试验引入损伤程度Ｄ表示材料低速冲击后材料参数的变化大小，通过准静态球面弯曲试验提出复合材料层合板抗冲击的三种表征参数：层内开裂临界能Ｅ１ｃ、层间开裂（分层）临界能Ｅ２ｃ、分层扩展阻力Ｒ．     

陶瓷/复合材料装甲板防弹机理分析

分析了纺织复合材料和陶瓷的低速冲击性能,并以此为理论基础,剖析陶瓷/复合材料装甲板受弹头冲击时的防弹机理,并建立此过程的动态分析模型,讨论和预测复合装甲的损伤和破坏,为复合材料在复合装甲上的应用和防弹能力预测提供理论分析依据。     

复合材料加筋板冲击后损伤容限研究

研究复合材料加筋板受冲击后的损伤演化具有较高的工程应用价值。首先,以某型无人机拟应用的复合材料加筋壁板(T300/BA9913)为研究对象,对其进行低速冲击试验;在壁板中央处和肋与壁板胶结处进行冲击,其冲击能量取6.67 J/mm,测量凹坑深度和分层损伤面积。然后,应用商业软件ABAQUS,编写相应的VUMAT子程序对冲击损伤进行模拟,软件中采用适宜的材料模型、单元种类并建立不同属性的接触,把基于应变的三维Hashin准则运用于复合材料单层板的损伤失效准则中去。最后,运用基于断裂韧度的连续的刚度退化方针对材料的刚度折减。将所建立的冲击模型的模拟结果与冲击试验数据进行对比,证明了冲击模型的有效性和准确性。     

Analysis of composite laminates with intra- and interlaminar damage

Failure process of composite laminate under quasi-static or fatigue loading involves sequential accumulation of intra- and interlaminar damage. Matrix cracking parallel to the fibres in the off-axis plies is the first intralaminar damage mode observed. These cracks are either arrested at the interface or cause interlaminar damage (delamination) due to high interlaminar stresses at the ply interface. This paper summarises recent theoretical modelling developed by the authors on stiffness property degradation and mechanical behaviour of general symmetric laminates with off-axis ply cracks and crack-induced delaminations. Closed-form analytical expressions are derived for Mode I, Mode II and the total strain energy release rates associated with these damage modes. Dependence of strain energy release rates on crack density, delamination area and ply orientation angle in balanced and unbalanced symmetric laminates is examined and discussed. Also, stiffness degradation due to various types of damage is predicted and analysed.     

一种交织铺层结构层合板性能

结合复合材料自动纤维铺放(AFP)技术,提出了一种交织铺层结构层合板成型方法,制备了非交织、交织正交层合板、非交织、两向交织和四向交织准各向同性层合板复合材料,并对交织铺层结构复合材料的层间结构和性能进行了分析研究。结果表明:交织正交层合板的拉伸、压缩、弯曲性能较非交织板性能均有所下降,但其层间剪切性能有明显提高,提高幅度约为16%;随着交织铺层组厚度的增加,交织层合板的拉伸性能呈下降趋势;交织层合板的开孔后拉伸、开孔后压缩和冲击后压缩强度保持率均高于非交织板,且冲击后分层损伤面积明显低于非交织板。交织铺层结构层合板相对于普通非交织层合板具有更好的损伤容限能力。     

混凝土房屋结构靶的超高速撞击特性研究

为了研究动能武器对混凝土类目标的毁伤效果,采用试验和数值仿真手段,对钨合金弹丸超高速撞击混凝土房屋结构靶进行了研究,探讨了混凝土房屋结构靶在超高速撞击条件下的毁伤特点。试验所用的钨合金弹丸重35g,长径比为5,撞击速度2．5km/s;混凝土房屋结构靶抗压强度34．4MPa。研究发现：在开展的试验条件下,房屋结构靶顶层板和底层板被穿透,未发生解体破坏;靶体中加筋对靶体的穿孔大小及结构破坏没有明显的降低作用;速度2．5km/s的弹丸经撞击40mm厚混凝土板后的速度降到2．0～2．3km/s 范围内;弹丸超高速撞击混凝土房屋结构顶层板形成的碎片云速度较高,部分碎片对人员具有较强的杀伤效果,该部分碎片的扩张角为23＆#176;,在底层板上的分布范围大于穿孔大小。