Phase Transformation in a β-Ti Alloy with Good Balance Between High Strength and High Fracture Toughness

This article studies the phase transformation of the metastable β-Ti-Al-Mo-V-Cr-Zr alloy (Ti-1300) to disclose the morphological reason for its high strength and high fracture toughness. It has been found that its ultrahigh strength (ultimate tensile strength exceeds 1 400 MPa) owes mainly to the spheroidization of the α-phase, while the high fracture toughness (exceeds 81 MPa·m^½) to the special lath-shaped α-particles. Compared to the needle-shaped second α-articles, the coarser lath-shaped ones remove the stress concentration at the lath tips and consequently benefit improvement of fracture toughness. The article also describes shape evolution of the α-particles during aging thermodynamically and kinetically, and suggests an optimized aging processing to achieve an ideal balance between high strength and high toughness for this alloy.     

预拉伸处理对2 A97薄板组织和性能的影响

通过室温拉伸、腐蚀试验、TEM等手段,研究人工时效前预拉伸处理对2A97铝锂合金组织和性能的影响。结果表明：在相同时效工艺下,经3%的预拉伸变形后,2A97合金的强度和耐蚀性能都有较大提高,其中抗拉强度提高了32 MPa,晶间腐蚀等级变为点蚀等级;预拉伸处理促进了时效过程中T1相在晶内的均匀弥散析出,降低了δ′相的含量,抑制了晶界平衡相的析出,从而改善了合金的强度和耐蚀性能。     

TC18钛合金普通退火工艺研究

研究了普通退火工艺参数对TC18（Ti-5A1-5Mo-5V-1Cr-1Fe）钛合金显微组织和力学性能的影响。结果表明,合金强度随退火温度升高先降低后上升,900％及以上温度退火后合金强度可达到1100MPa以上。a相形状、数量及尺寸等方面的变化是影响合金强度和塑性的关键因素。     

新型Al-Zn-Mg-Cu合金双级时效制度研究

采用硬度法测定了一种新型Al-Zn-Mg-Cu合金挤压带板的GP区临界形核温度TV（GP区在此温度下形核不依靠空位浓度）和TC（GP区在此温度以上不能形核）。他们的温度区间分别为130～140℃和170～180℃。依据实验结果确定了合金的一级时效温度为120℃,二级时效温度为165℃。合金在120℃/4h+165℃/8h制度下热处理后,L向的抗拉强度、屈服强度、伸长率、断裂韧度和电导率分别为617MPa,590MPa,13.5%,41.6MPa m^1/2和39.1%IACS,是一种综合性能优良的双级时效600MPa级铝合金。     

时效处理对高强耐热镁合金等温模锻件组织与性能的影响

采用锻后直接时效处理的方法研究了时效处理工艺对高强耐热镁合金等温模锻件的组织与性能的影响,分析了其时效强化过程中第二相的形成及时效处理制度相关的断裂行为,得出了其时效强化的内在机理及优化的锻后时效制度.研究表明优化的时效处理制度为200℃×63 h.在该时效制度下,材料的室温抗拉强度达到了371MPa,屈服强度达到243 MPa,伸长率达4.1％     

BNi-2非晶钎料钎焊高铌TiAl合金与GH3536合金接头组织与性能

采用非晶态BNi-2钎料成功实现了高铌TiAl合金与GH3536合金的连接,获得良好的钎焊接头。钎焊接头的典型界面组织为TAN/B2+τ3/τ4+（Ni-Ti）-B/γ+（Ni-Ti）-B+CrB+G相/GH3536。通过分析钎焊温度对接头界面微观组织的影响,表明BNi-2钎料中B元素的扩散以及GH3536合金向液态钎料中的溶解对界面组织结构演变起着至关重要的作用。而随着钎焊温度的升高,扩散IV区逐渐消失,接头由4个区域变为3个区域,τ3/τ4化合物层及钎缝区域均逐渐增厚,黑色CrB相发生粗化,细小点状（Ni,Ti）-B含量减少。1 160℃保温10 min时,所获得的钎焊接头最大室温及高温（700℃）抗剪强度分别为~106.8 MPa和~76.2 MPa,其剪切强度降低约28.6%,接头均呈现脆性断裂模式。接头形成过程可以划分为固相扩散、液相生成、等温扩散凝固和残余液相析出4个阶段。     

ZL101泵壳凝固成形工艺设计数值仿真优化

针对ZL101泵壳设计了两种不同的浇铸系统,借助FEM方法完成了充型流动场、凝固固相场与疏松分布的数值计算对比分析。结果表明:采用底注式浇铸系统,合金熔体充型平稳,型腔内部充型初期卷入的气体可有效排出,凝固次序为自上而下与自内向外的逐层凝固,T5热处理后本体试样平均抗拉强度、屈服强度与延伸率分别为334.5、274 MPa与5.8%,满足了HB962-2001Ⅱ类铸件的技术指标要求。     

低Cu含量Al-Mg-Si-Cu合金的T78双级时效

采用拉伸和加速腐蚀试验,分别测试了预时效（180℃）+再时效（190、200、210℃）对一种低Cu含量Al-Mg-Si-Cu合金拉伸性能和晶间腐蚀的影响,结果表明,延长预时效和再时效时间或提高再时效温度,合金强度逐渐降低,同时,腐蚀类型按晶间腐蚀→均匀腐蚀→坑蚀顺序演化。其中,经预时效（180℃/2~8 h）+再时效（200℃/6 h或210℃/2 h）处理,合金抗拉强度、屈服强度和延伸率分别为380~395 MPa、360~380 MPa和12%~15%,腐蚀类型为均匀腐蚀,实现强度与耐蚀性的良好配合。透射电镜观察表明,随着双级时效程度的增加,合金强度的降低源于基体β"相的减少及β'相和Q'相的增加;晶间腐蚀倾向的降低与晶界Q相大间距、断续分布有关;坑蚀的形成则与结晶Q相吸收周围析出相、形成基体无析出区有关。     

激光熔化沉积TA15+Ti_2AlNb合金的组织与力学性能

将TA15和Ti_2AlNb合金粉末以不同比例预混,采用激光熔化沉积工艺,制备出40%TA15+60%Ti_2AlNb,50%TA15+50%Ti_2AlNb,60%TA15+40%Ti_2AlNb(质量分数)3种比例的合金薄壁,分析了薄壁的成分、组织及力学性能。结果表明:3种沉积薄壁的成分分布均匀,合金由α相、α2相及β/B2相组成,针状α相和α2相呈网篮状分布在初生β/B2晶粒内部;3种合金的抗拉强度分别为1108 MPa,1071 MPa,1105 MPa,断裂伸长率分别为3.0%,2.2%,3.8%;拉伸断口可见沿α2相撕裂产生的撕裂棱,断裂方式均为准解理断裂。     

高强耐热铸造铝硅合金的试验研究

 优化了一种高强耐热铸造铝硅合金的化学成分,确定了合理的热处理工艺,分析了该合金的强化、耐热机理。此合金具有优良的铸造性能,其机械性能：室温σｂ≥３００ＭＰａ,δ≥３％；２５０℃σｂ≥２００ＭＰａ、δ≥４％。可提供优质导弹舱体等铸件的生产。     

退火态ZTi6Al4V铸造钛合金的断裂韧度研究

将尖切口强度理论用于ZTi6Al4V铸造钛合金损伤容限性能的评价,探讨了不同退火温度对其三点弯曲断裂韧度KQ的影响。结果表明:尖切口试样测定的断裂韧度KQ1不等同于标准试验方法测定的KQ,但可用于铸造钛合金不同工艺间断裂韧度的比较。退火温度的改变可微调ZTi6Al4V铸造钛合金的强度和断裂韧度,在700℃或820℃保温2h退火处理,试样的断裂韧度较好,KQ值分别达到78.11 MPa.m1/2和79.44MPa.m1/2,屈服强度分别为782.74MPa和771.49MPa,抗拉强度分别为860.18MPa和853.0MPa,伸长率达8.10%和7.46%,获得了较好的强塑性匹配。     

少量Cu对喷射沉积Al-Li合金显微组织与性能的影响

用喷射沉积方法制备了Al-Li合金及其含0.5%Cu的改型合金,进行了挤压和时效处理,测定了不同状态下这两种合金的显微组织和室温拉伸性能。结果表明,喷射沉积状态的Al-3.8Li-1.0Mg-0.4Ge-0.2Zr合金具有等轴细晶组织,析出Al4Li9和δ AlLi相,时效后析出大量δ' AlLi相;添加0.5%Cu使屈服强度提高30～48MPa,拉伸强度提高44MPa,性能提高的原因是Cu的固溶强化和Li在基体固溶度减少导致δ'相含量增加。     

Al/Ni含能多层膜在Al2O3陶瓷/不锈钢焊接中的应用

采用磁控溅射设备,生长AuSn合金做焊料层、Al/Ni含能多层膜做热量提供层,实现了不锈钢和Al_2O_3间的异质材料自蔓延高温扩散焊。利用SEM、XRD和DSC等测试手段表征AuSn合金和Al/Ni含能多层膜的微观形貌、相成分和放热量;用万能试验机测试焊接接头的力学性能。结果表明,AuSn合金的质量比基本达到80∶20,而多层膜的层状结构清晰,反应热达到1 239 J/g。焊接实验结果表明,仅使用AuSn焊料时,剪切强度仅为46 MPa,在增加Al/Ni含能多层膜后,其剪切强度可达90 MPa,强度提高了约一倍。焊接接头的界面显微形貌和相结构研究表明,剪切强度的增强主要是Al/Ni多层膜提供了额外能量使得界面处的反应剧烈,陶瓷金属化层与中间层的反应加剧,形成了新的反应生成物。     

电镀硬铬工艺对TC6钛合金性能的影响研究

研究了电镀硬铬工艺对TC6钛合金的影响,利用氢测定仪、拉伸试验机、疲劳试验机等设备对镀铬后TC6钛合金的氢含量、力学和疲劳等性能进行了研究。结果表明:TC6钛合金电镀硬铬后基体氢含量显著提高,氢含量合格但接近上限,不能通过氢脆实验。建议TC6钛合金电镀硬铬工艺不应用在高应力集中及高承载部位,以避免氢脆发生。抗拉强度基本不变,伸长率和断面收缩率有所降低,分别降低17.3%和24.0%。TC6钛合金电镀硬铬后由于镀层造成的残余拉应力,使得疲劳极限显著降低,由626.0MPa降低至201.3MPa。     

热等静压温度对K447A高温合金显微组织及性能的影响

研究了热等静压温度对K447A合金显微组织及性能的影响。测试了合金的持久性能和室温拉伸性能。利用金相显微镜(OM)和扫描电镜(SUM)观察了合金显微组织。结果表明,1185～1210℃/180MPa/4h(+1185℃/2h,AC+1100℃/4h,AC+870℃/20h,AC)下,随热等静压温度的提高,合金中显微疏松逐步闭合,碳化物逐步细化和球化;γ-γ’共晶相尺寸和数量逐步减小,共晶特征趋于不明显;晶界呈不连续颗粒状;存在大、小两种尺寸的γ’相。经1185～1210℃HIP处理的合金980℃/200MPa持久性能大幅提高;经1195℃HIP的合金760℃/724MPa持久性能达到最高。经1210℃HIP处理的合金980℃/200MPa持久性能达到最高。180MPa/4h条件下,K447A合金合适的热等静压温度为1185～1210℃。     

喷射沉积制备Al-Zn-Mg-Cu合金大型坯组织性能的研究

利用Ospray公司的喷射沉积设备制备了Al11.3Zn2.4Mg1.1Cu合金,合金挤压成棒材后,经过固溶和时效处理,用万能材料实验机对其进行了力学性能测试,合金的抗拉强度为849 MPa、屈服强度为796 MPa,延伸率为3.3%.透射电镜和扫描电镜对拉伸试样微观组织的研究结果表明,合金微观组织中包括微米级晶粒和纳米级晶粒,合金的强化方式为纳米晶强化、固溶强化以及沉淀强化,拉伸试样的断口分析表明,合金的断裂方式主要为沿晶断裂.     

新型高强铝锂合金热变形工艺及其变形后的组织性能

研究了锻造温度、锻造比等对新型高强铝锂合金成形质量的影响,总结了新型高强铝锂合金在不同锻造比下的组织性能变化规律.结果表明:锻造比为3～7时,合金热处理后径向抗拉强度均大于500 MPa,并且其径向抗拉强度明显高于轴向;并且随着锻造比的增大,晶粒尺寸也逐渐增大.     

热处理制度对激光增材制造TA15钛合金力学性能的影响

进行了普通退火态和双重退火态激光增材制造TA15钛合金显微组织观察和力学性能试验。试验结果表明:普通退火态为细片层α+β超细网篮组织,双重退火态为端部带根须状形貌的初生α相+超细β转变组织构成的特种双态组织;普通退火态激光增材制造TA15钛合金极限强度、屈服强度和疲劳极限均优于双重退火态;双重退火态激光增材制造TA15钛合金具有较好的塑性和优异的断裂韧性。     

Mg/Al合金粉末热压烧结中相变扩散过程研究

利用OLYMPUS GX71金相显微镜及EDS对Al-15％Mg热压烧结样品进行金相显微组织观察与成分分析,探讨烧结过程中组织演变过程。实验结果表明：热压烧结过程中两种粉体发生互扩散,首先在Mg颗粒边缘形成γ（Al12Mg17）相,而后随扩散的进行γ相转变为β（Al3Mg2）相,Mg颗粒由外向内不断的形成γ相,而后不断的转变为β相,直到全部生成β相。随温度的降低,β相会以极其细小的颗粒形式析出;利用真空热压烧结方法在420℃,150Mpa下保压3—4h进行固相烧结获得密度低于2．5g／cm^3致密度达98％以上的Al—15％Mg合金。     

EB-PVD热障涂层对IC10合金力学性能的影响

采用电弧离子镀技术在IC20合金基体上制备NiCrAlYSi粘结层,利用电子束物理气相沉积（EB—PVD）技术在粘结层上制备YSZ陶瓷面层。研究了YSZ热障涂层对IC10合金拉伸、持久、疲劳性能的影响。结果表明：IC10合金沉积YSZ热障涂层后,980℃／200MPa高温持久寿命与IC10合金相当;900℃高温抗拉强度σb、屈服强度σ0.2、伸长率占和断面收缩率砂与基体相比,基本保持不变;室温抗拉强度σb。屈服强度σ0.2：与基体相比稍有下降;800℃／447MPa疲劳寿命与基体合金相当。因此,IC10合金沉积TBCs涂层后,对IC10合金力学性能无明显影响,不影响合金的实际使用。