无纺布织物涂层的吸波性能

以无纺布为基材,采用叠层式结构制备无纺布织物涂层吸波材料。用3 cm波导测量系统在9.35GHz研究复合吸波剂(羰基铁粉和乙炔炭黑)含量和叠层结构对材料吸波性能的影响。结果表明,这种以无纺布为基材的吸波材料,通过控制吸波涂层的组成和设计合理的结构,增加入射电磁波与吸波材料的作用几率,可以改进材料的吸波性能并降低材料面密度。     

耐高温抗激光烧蚀涂层研制与性能表征

以有机硅树脂、聚碳硅烷和玻璃粉为黏结剂,添加Al2O3,BN,SiC,ZrO2,SiO2和碳纤维等耐热填料制备了抗烧蚀涂层,对其物理机械性能进行了表征,同时分别采用马氟炉、氧乙炔焰烧蚀对其耐热抗烧蚀性能进行了表征。研究结果表明:玻璃粉、BN对改善涂层裂纹起关键作用,ZrO2对提高涂层隔热和耐烧蚀性能至关重要。所研制涂层在厚度为1mm的30CrMnSiA钢基材表面涂覆600μm,经受3000℃氧乙炔焰4s烧蚀,钢基材不发生穿孔;900μm厚度的涂层在531W/cm2激光功率密度下照射4s,带涂层钢基材背面温度比同等辐照温度下,空白钢板背面温度下降1000℃左右。     

成果简介

1　ＫＹ— 5应变胶粘剂本成果研制的应变胶可粘结金属与非金属材料 ,可作为电气元件的绝缘涂层、防潮涂层 ,在国内最先解决了聚酰亚胺应变片的粘结问题。胶主体选用锌酚醛树脂 ,取消固化剂 ,研制成单组分应变胶。在 10 %稀酸、稀碱及一般无机介质中浸泡 2 4ｈ以上强度不下降 ,应变极限可达 2× 10 4 με以上 ,疲劳寿命达 10 7次。使用温度 - 190℃～ 180℃ ,绝缘强度达10 5ｍΩ ,耐腐蚀性能良好。本成果有推广应用价值。2　高精密石英谐振器金锗焊本成果金锗焊高精密晶体的优点是 :由于采用新工艺而避免了锡焊工艺的松香污染 ,结构耐温从12…     

陶瓷前驱体基高温高辐射涂层制备及表征

以陶瓷前驱体树脂为成膜物,以过渡金属氧化物和硼化物为填料,采用空气喷涂工艺在镍基高温合金和C/C基材上制备出了高温散热性能好、抗热震性好的高温高辐射涂层,并用DSC-TG、光学显微镜和风洞对涂层性能进行表征。结果表明:该涂层室温~827℃发射率达到0.85~0.92,827℃~室温抗热震循环20次后涂层不剥离、不脱落;该涂层在290 k W/m2冷壁热流、300 s时长的风洞考核条件下,可将镍基高温合金基材温度从686℃降到646℃,降温40℃。     

TC4钛合金表面激光原位反应制备TiN涂层及性能研究

利用激光原位反应技术在TC4钛合金表面制备了无裂纹、组织均匀致密的TiN涂层,并分析了激光氮化层的显微组织、成分和物相,测试了涂层横截面显微硬度、涂层耐磨性能及抗SiO_2颗粒高速冲蚀的能力。结果表明:在适当的激光参数下制备的氮化钛涂层与TC4基体之间呈现良好的冶金结合,其界面结合强度为240～270MPa;涂层主要为硬质TiN相,涂层硬度高达1550HV_(0.1),约为基材的4.5倍;涂层磨损失重量是TC4钛合金的14.7%;在60o冲蚀角度下,基材的冲蚀质量损失为涂层的2倍。     

钛合金基体激光熔覆WC/TC18复合涂层滚动接触疲劳性能研究

为了提高钛合金的滚动接触疲劳性能,以碳化钨(WC)/钛合金(TC18)混合粉末为原料,利用激光熔覆技术在TC18基材表面制备了耐磨涂层,分析了涂层的显微组织和显微硬度,在室温条件下测试了涂层的接触疲劳性能.结果表明,涂层与基体冶金结合良好,WC颗粒呈不规则块状均匀分布于β-Ti基体中,WC显微硬度在2122～2271H...     

镁合金表面冷喷涂420不锈钢/WC-17Co涂层及其耐磨耐蚀性能

采用冷喷涂工艺在AZ80镁合金表面制备420/WC-17Co涂层。利用SEM分析喷涂粉末形貌及涂层显微结构;通过显微硬度计和万能材料试验机测定涂层的显微硬度和结合强度;采用球盘式摩擦磨损试验机考察涂层的摩擦磨损性能;通过电化学实验测定涂层和镁合金基材的耐腐蚀性能。结果表明:采用冷喷涂工艺可在AZ80镁合金基体上制备出高质量的420/WC-17Co涂层,冷喷涂420/WC-17Co涂层的显微硬度为(615±62)HV,结合强度为(57±11)MPa,涂层的磨损率为3.3×10~(–6) mm~3·N·m,其耐磨性较镁合金基材提高了2个数量级,涂层自腐蚀电流较镁合金基材降低了1个数量级。因此,冷喷涂420/WC-17Co涂层在不产生明显热影响的情况下,可以显著提高镁合金表面的耐磨耐蚀性能,是一种较为理想的镁合金表面强化工艺。     

一种弹性低密度耐高温隔热涂层

针对固体火箭发动机实际使用的热环境要求,研制了一种弹性低密度耐高温隔热涂层,通过石英 灯辐射和电弧风洞试验对其进行了防热性能考核。该涂层密度为0. 62 g/ cm3,伸长率为25%,热导率为0． 18 W/ (m·K);在401℃时DSC 失重率仅为6. 6%;验证考核表明,采用1. 0 mm 涂层时,壳体与涂层界面温度最高 为77. 3℃,壳体背温度最高为44. 5℃。     

防静电白色热控涂层的耐空间环境及工艺性能

研究了防静电白色热控涂层（ACR-1）的耐空间环境性能及工艺性能。在模拟空间环境设施中研究了紫外辐照、电子辐照和质子辐照对涂层太阳吸收率（αs）的影响。结果表明ACR-1在地球静止轨道环境中具有较高的稳定性；经过3000当量太阳小时（ESH）的紫外光辐照后，△αs为0．02；质子辐照效应对涂层仅。的变化影响较大。另外，研究了涂层厚度对αs和其与基材结合力的影响，以及基材表面处理工艺对涂层在-196—150℃冷热交变循环试验中可靠性的影响。     

激光熔覆Ni16Ti6Si7涂层组织与耐磨性

以Ni—Ti—Si合金粉末为原料，利用激光熔覆技术在0Cr18Ni9奥氏体不锈钢基材上制备了以Ni16Ti6Si7初生树枝晶和枝晶间γ-Fe—Ni固溶体组成的耐磨涂层。用光学显微镜、扫描电镜、透射电镜等对涂层组织进行了分析，测试了其在高温干滑动条件下的磨损性能。结果表明，由于Ni16Ti6Si7较高的硬度和具有较好韧性配合的涂层组织，激光熔覆涂层具有优异的高温磨损性能。     

含氢 WC/ C 复合涂层在不同润滑油环境的摩擦性能

利用非平衡磁控溅射技术,通过同时离化乙炔气体和共溅射石墨靶与碳化钨靶,在304不锈钢和单晶硅基底上沉积具有Cr过渡层和WC过渡层的含氢WC/C复合涂层。采用扫描电镜、Raman光谱仪、X射线衍射仪、纳米压痕仪等对涂层的微观结构、力学性能进行分析。利用Rtec摩擦磨损试验机对WC/C复合涂层与304不锈钢基底在PAO基础润滑油环境、发动机润滑油环境以及腐蚀性发动机润滑油环境进行摩擦性能测试。结果表明:涂层内含有较多类石墨sp2键,WC1-x相镶嵌在非晶碳基质中构成多相复合结构;涂层的硬度和弹性模量明显高于304不锈钢基底,且其H/E值远高于基底;与304不锈钢基底相比,在三种润滑油环境下涂层均具有较低的摩擦因数和磨损率。     

ZrB2 及其复合陶瓷的高温抗氧化性能

综述了ZrB_2及其复合陶瓷的高温氧化行为,认为ZrB_2陶瓷是一种优异的高温结构材料,其氧化失效是由于氧化产物B_2O_3保护层挥发失效而导致的;二元陶瓷ZrB_2-SiC由于SiC的加入,高温抗氧化性能大大提高,并对其在不同温度下的氧化物结构进行了阐述。在此基础上提出了进一步提高ZrB_2-SiC陶瓷抗氧化性能和服役温度的方法,并以添加TaC和LaB_6形成三元复相陶瓷为例进行了说明。     

高温热管与高导热石墨烧蚀传热性能

利用石英灯辐射加热器和电弧风洞耦合加热模拟高超声速飞行器驻点高温区的加热环境,对一

种内部为高温热管和一种内部为高导热石墨的简单球柱形套装样件进行了加热试验。利用非接触红外测温装

置对样件表面的温度进行了测量,通过与内部为C/ C 材料制成的对比样件的试验结果分析,发现高温热管和

高导热石墨均能够有效地将样件驻点高温区热量传导到柱身低温区,其中高温热管样件驻点温度降低9. 5%,

柱身温度升高14. 6%;高导热石墨驻点温度降低14. 4%,柱身温度升高11. 4%,显示两种材料均具有良好的热

疏导效果。

     

Effect of boron doping on waterproof and dielectric properties of polyborosiloxane coating on SiO2f/SiO2 composites

A hydrophobic coating of the silica fiber reinforced silica composites (SiO_2f/SiO₂) was synthesized by sol-gel method using methyltriethoxy-silane (MTES) and boric acid (B(OH)₃) as raw materials. The relationship among boron doping, chemical structure of precursors and durability of hydrophobic coatings was discussed. The Si-O-B and methyl groups were successfully introduced in the gel precursors according to the FT-IR and XPS results. The resins were filled in the internal and surface holes of the SiO_2f/SiO₂ composites partially or completely, which is beneficial to reduce the physical adsorption of the moisture. In addition, hydroxyl groups of the SiO_2f/SiO₂ composites reacted with the resins and hydrophobic methyl groups were introduced, leading to the reduction of the chemical adsorption of water. Also, the boron doping was beneficial to enhancing the physical cross-linking between the coating and the SiO_2f/SiO₂ composites, and improved the adhesion of the coating to the substrate. The results show that the optimal hydrophobic coating with contact angle 130.33°, moisture absorption 0.33% and adhesion level 1 is obtained when the molar ratio of MTES to B(OH)₃ is 10:4. The real permittivity of M10B4 is constant in the range of 2.32–2.51 and the dielectric tangent loss is constant in the range of 5.5 × 10⁻⁴–8.7 × 10⁻³. The hydrophobic coating has excellent dielectric properties.     

固化工艺参数对复合材料补片温度场的影响

基于热传导定律和固化动力学理论,建立了热固性树脂基复合材料固化过程的三维有限元模型,通过与文献实验结果的比较,验证了该模型具有较高的可靠性。采用该模型计算了AS4/3501层合板挖补修理固化过程的温度场和固化度场,并分析了固化温度及升温速率对补片中心点温度场和固化度场的影响。结果表明:在固化反应的起始阶段,固化温度和升温速率对补片温度和固化度的影响很小;随着固化反应的进行,固化温度和升温速率对补片温度和固化度的影响越来越大;在第二次升温阶段初期,固化温度对补片中心点温度的影响又逐渐缩小;在每次保温阶段末期,补片温度和固化度不再受升温速率的影响。     

石墨含量对PEEK基复合涂层性能的影响

利用石墨和聚四氟乙烯(PTFE)对聚醚醚酮(PEEK)进行混杂改性,控制PTFE和PEEK的质量比不变,通过冷压烧结的方法在不锈钢表面制备不同石墨质量分数的PEEK基复合涂层,研究石墨含量对涂层力学和摩擦性能的影响。结果表明:随着石墨质量分数的增多,PEEK基复合涂层的结晶度逐渐下降,涂层的硬度先增高后降低,摩擦因数不断降低,磨损率先降低后上升。在石墨质量分数为4%时,硬度最高21.78HV,摩擦因数为0.0461,磨损率最低为2.06×10~(-6)mm~3/(N·m),这与之前的研究相比,涂层的耐磨性得到大幅提高。但是过高的石墨质量分数会使分子链柔顺性下降、链段运动降低,涂层的耐磨性大大降低。     

耐高温隔热材料组合结构模拟研究与试验验证

以热防护系统隔热组合结构中不同隔热材料厚度尺寸为计算变量,以飞行器主结构温度极值即最低背面温度为目标参数,以组合结构中第二层材料最高使用温度为约束条件建立隔热组合结构模型,并进行了石英灯考核验证。采用通用软件ANSYS 进行一维瞬态有限元热分析,将模型计算结果和试验结果进行了全面对比,各项数据吻合良好。     

高阻尼复合材料支撑筒结构设计与材料工艺

支撑筒用于运载火箭与卫星之间的连接,支撑筒的阻尼减振效果决定了卫星能否正常工作。T700S/AG80复合材料制备的某支撑筒无法满足室温阻尼性能要求。本文通过两种途径提高了支撑筒的阻尼性能,第一种途径采用环氧丁腈预聚物861340共混改性AG80环氧树脂,当861340含量为23%时,改性树脂的阻尼性能最佳;第二种途径是对支撑筒进行分段铺层设计。共制备两个支撑筒1#和2#,1#采用未改性复合材料,2#采用阻尼改性复合材料以及分段铺层,在纵向振动试验中,与1#结构振动响应相比,2#结构的响应下降了60.5%;在横向振动试验中,与1#结构振动响应相比,2#结构的响应下降了20.7%。     

混杂纤维复合材料层板的抗弹冲击性能

为了考察混杂纤维复合材料层板的抗弹冲击性能,采用碳纤维织物或玻璃纤维织物与芳纶纤维织物复合材料层共固化的方式,利用热压罐成型工艺制备了几种具有不同面密度及铺层结构的混杂纤维复合材料层板,并进行抗弹冲击性能测试、表观形貌观察和无损检测分析。结果表明:纯芳纶纤维及混杂纤维复合材料层板的钢弹冲击破坏模式相同,均为表层剪切破坏,中间层分层破坏,背层拉伸断裂破坏;层间混杂顺序对复合材料层板的分层缺陷面积有较大影响,当碳纤维层作为背层时,层板的分层缺陷面积为12 863. 6 mm2小于玻璃纤维层作为背层时(17 400. 5 mm2);当芳纶层作为背板时,混杂纤维复合材料层板冲击后分层缺陷面积与纯芳纶的相当(14 151. 0～14 927. 0 mm2)。混杂纤维复合材料对层板的抗弹冲击性能有较大影响,混杂后复合材料的弹道极限速度(v50)均有一定程度的提高,其中玻璃纤维/芳纶复合材料的v50从纯芳纶复合材料层板的193. 08提高至204. 33 m/s。将碳纤维层或玻璃纤维层作为着弹面层的混杂纤维复合材料层板具有更优异的抗弹冲击性能,其贯穿比吸能(BPI)均优于纯芳纶复合材料层板。     

防止 C/C 复合材料氧化的 MoSi2/SiC 双相涂层系统的研究

 由固相扩散-浸渗处理制备了防止碳/碳复合材料氧化的MoSi2/SiC双相涂层。通过对涂层的结构、成份以及氧化机理的研究表明，MoSi2/SiC双相涂层由内层为β-SiC和外层为MoSi2/SiC双相层构成，具有优异的高温抗氧化性能。