基体曲率对热障涂层结合强度影响的无损检测研究

 针对复杂型面航空发动机涡轮叶片表面热障涂层(TBCs)的失效问题,采用交流阻抗谱(IS)法和洛氏硬度(RH)压痕法对比研究了制备在平板基体和曲率基体上,热障涂层在热循环过程中微观结构和界面结合强度的演变规律。交流阻抗谱法的结果表明:两种涂层试样的热生长氧化(TGO)层厚度及陶瓷层内裂纹数量均随着热循环时间增加而增长,但曲率试样的微观结构恶化速度更快;洛氏硬度压痕法的结果验证了经热循环后,曲率基体上热障涂层界面结合强度低于平板样品。     

电子束物理气相沉积LaZrCeO热障涂层微结构与热循环性能

热障涂层(thermal barrier coatings,TBCs)是一种由金属黏结层、热生长氧化物层和陶瓷面层组成的金属-陶瓷复合系统,在先进的航空发动机领域上引起了广泛的关注,但目前先进热障涂层的热循环寿命提升和失效行为研究仍然是一个难点。本研究采用电子束物理气相沉积技术(electron beam physical vapour deposition,EB-PVD)制备LaZrCeO/YSZ双陶瓷层热障涂层,研究热障涂层的相结构、显微组织和失效行为。结果表明:LaZrCeO/YSZ涂层为烧绿石与萤石结构组成的复合涂层材料,LaZrCeO/YSZ涂层的微观结构由羽毛状纳米结构和柱内孔隙组成;在1100℃热循环条件下,LaZrCeO/YSZ双陶瓷层热障涂层展现了良好的热循环寿命;热循环实验后,由于应力累积的作用裂纹在热生长氧化层(TGO)中萌生并扩展,包括水平裂纹和垂直裂纹两大类,进而引起整个涂层体系的不稳定,最终导致涂层失效。     

粘结层表面预处理对EB-PVD热障涂层循环氧化的影响

研究了在Ni3Al基高温合金基底上采用阴极电弧镀方法制备NiCoCrAlYHf粘结层、电子束物理气相沉积(EB PVD)方法制备Y2O3 ZrO2陶瓷层的热障涂层(TBCs)在1150～30℃之间的热循环氧化行为。通过对热循环过程中热障涂层界面韧性的测试和氧化行为的研究,分析了粘结层表面预处理工艺(喷丸和吹砂)对热障涂层使用寿命的影响。由于喷丸和吹砂会降低热障涂层的界面韧性,同时又促进了热生长氧化物(TGO)的生长,这些预处理工艺不利于提高热障涂层的寿命。     

电子束物理气相沉积热障涂层陶瓷层微裂纹形成机理的研究

采用电子束物理气相沉积方法制备热障涂层，对其在热循环过程中陶瓷层产生的裂纹进行了观察。结果表明，陶瓷层中的裂纹起源于陶瓷层与金属粘结层的界面处，该处存在着不同于界面其他处的氧化物。应力计算结果表明，陶瓷层中产生的微裂纹不仅仅是陶瓷／金属界面间的热应力所致，还与产生的氧化物的种类有着密切的关系。     

EB-PVD方法制备热障涂层热循环性能研究

采用电子束物理气相沉积(EB-PVD)技术在不同基体预热温度条件下制备NiCoCrAlY粘结层和氧化钇部分稳定的氧化锆面层。对样品进行了热循环试验。观察热循环过程中热障涂层显微结构的变化并分析了连续恒温氧化与热循环氧化间的差异,提出了EB-PVD热障涂层热循环的失效机理。     

氧化锆基陶瓷热障涂层的研究进展

氧化锆基陶瓷热障涂层是航空发动机的关键技术。根据一元氧化物、二元氧化物和多元氧化物掺杂稳定二氧化锆(ZrO_2)热障涂层的相关研究报道,系统地总结了氧化锆基陶瓷热障涂层在相稳定性、服役温度、热循环寿命、热导率、热膨胀系数等方面取得的进展;在此基础上,指出了氧化锆基陶瓷热障涂层的未来研究与发展方向。     

稀土氧化物改性氧化锆/铂铝热障涂层的制备及其高温性能

针对我国某型航空发动机涡轮叶片用DZ125与DZ406高温合金,开展了稀土氧化物改性氧化锆/铂铝热障涂层体系的制备工艺及涂层高温性能研究。采用电镀Pt和气相渗铝的工艺制备了PtAl金属粘结层,研究了镀Pt前处理、不同镀Pt层厚度以及渗铝温度等关键工艺参数对涂层的微观结构和抗高温氧化性能的影响规律。采用优化后的涂层工艺制备的PtAl粘结层在1150℃时的抗氧化性能优异。采用电子束物理气相沉积（EB–PVD）在PtAl粘结层表面制备了稀土氧化物改性的氧化锆（GYb–YSZ）陶瓷涂层。由GYb–YSZ和Pt Al组成的热障涂层在1050℃热循环4320次（1050℃保温时间720 h）后,涂层表面状态完好,未发现明显剥落现象,表明该热障涂层体系具备良好的热循环性能。     

盐雾腐蚀对热障涂层高温循环氧化性能的影响

利用电子束物理气相沉积法在Ni基高温合金表面制备了(ZrO₂＋MCrAlY)双层结构热障涂层。研究了常温盐雾腐蚀对其循环氧化行为的影响。试验结果表明涂层经过常温盐雾腐蚀后,陶瓷层的裂纹发生扩展,氧化锆晶体挤压、变形,同时由于常温盐雾环境的作用导致涂层在高温氧化过程中粘结层氧化严重,生成的热生长氧化层产生较大的体积膨胀效应,导致应力集中,降低了涂层的高温循环氧化性能,缩短了涂层的寿命。     

真空预氧化处理对热障涂层静态氧化行为的影响

利用超音速火焰喷涂技术在DZ40M合金表面制备了Ni Co Cr Al Y粘结层,采用等离子喷涂技术在粘结层表面制备了陶瓷面层,并对整体热障涂层进行了真空预氧化处理。通过高温静态氧化实验研究了真空预氧化对热障涂层的氧化行为的影响。结果表明:真空预处理可在MCr Al Y粘结层和陶瓷面层的界面处形成连续、致密的α-Al2O3层;在1050℃下氧化800h后,喷涂态涂层TGO中除α-Al2O3外,还生成了大量尖晶石氧化物,而预氧化涂层TGO则以α-Al2O3为主;预氧化处理有效抑制了涂层在高温氧化过程中尖晶石氧化物的形成,从而降低了整体氧化膜的生长速率。     

双陶瓷层热障涂层3.5％Y2O3-La2(Zr0.7Ce0.3)2O7/YSZ研究

采用EB-PVD沉积了3.5％Y2O3-La2(Zr0.7Ce0.3)2O7(3.5Y-LZ7C3)/YSZ双陶瓷热障涂层,分析了涂层的成分、相结构、组织形貌和热循环氧化性能.研究表明:La2(Zr0.7Ce0.3)2O7(LZ7C3)材料中掺杂Y2O3能有效地降低涂层中La2O3/ZrO2/CeO2的成分偏差;双陶瓷涂层在1050℃下氧化增重动力学为M=0.1219t1/3,相比抛物线型YSZ涂层的氧化增重曲线,较大减缓了氧化速度;沉积态双陶瓷涂层表面结构(即3.5Y-LZ7C3涂层结构)为烧绿石结构,经过热循环后逐渐分解,出现了萤石结构以及La2O3的衍射峰;在1050℃双陶瓷层热循环氧化寿命达768h.     

大气等离子喷涂热障涂层高温氧化行为研究

采用等离子喷涂工艺在GH4099合金基体上制备了热障涂层,并进行了1050℃恒温氧化试验,综合利用X射线衍射仪、扫描电子显微镜、能谱分析仪等检测手段,分析了涂层的显微结构及高温氧化行为。结果表明：等离子喷涂（APS）热障涂层在高温氧化过程中,黏结层被氧化生成热生长氧化物（TGO）。但长时间氧化后,在与TGO毗邻的金属黏结层中产生了范围较窄但浓度变化较大的贫Al带,TGO层出现保护性Al2O3向非保护性混合氧化物转变的现象,导致致密Al2O3层的连续性被破坏,TGO厚度快速增加。     

交流阻抗谱法评价热障涂层的热腐蚀行为(英文)

本文利用交流阻抗这种无损检测的方法研究了热障涂层在质量分数为25%NaCl+75%Na2SO4混合盐体系中的热腐蚀行为。实验结果显示,热腐蚀条件下,在陶瓷层和粘结层界面处形成TGO层为混合氧化物层,成分为Cr2O3、(Ni,Co)(Cr,Al)2O4和NiO,其厚度增长符合抛物线规律。热障涂层在110个循环腐蚀之前时,TGO层的电阻值随其厚度的增加而增加;110个循环后,虽然TGO层的厚度还是在增加,但由于TGO层孔隙的增多而导致其电阻值有所下降。陶瓷层的电阻值随着陶瓷层中裂纹的萌生和扩展而不断增大。等效电路中得到的参数可以用来表征热障涂层的失效行为。     

梯度热障涂层的设计

 采用电子束物理气相沉积方法 (EB PVD)制备了梯度热障涂层,其结构设计为NiCoCrAlY粘结层 /Al₂O₃ YSZ过渡层 /YSZ陶瓷层。YSZ陶瓷层的结构为柱状晶结构,Al₂O₃ YSZ梯度过渡层为梯度微孔结构。采用有限元方法对梯度热障涂层进行热应力分析,优化了Al₂O₃ YSZ梯度过渡层的组成。计算结果表明,梯度涂层的内应力显著降低,而且界面及其附近应力和应变变化较平缓。过渡层厚度的增加有利于降低涂层内应力和缓和涂层界面处的应力集中。     

Effects of Shot Peening Process on Thermal Cycling Lifetime of TBCs Prepared by EB-PVD

Conventional two-layered thermal barrier coatings (TBCs) are prepared by electron beam physical vapor deposition (EB-PVD) with ZrO2-8 wt% Y2O3 (8YSZ) as top coat and CoCrAlY as bond coat on disk-shaped Ni based super-alloy. In this paper, three kinds of shot peening process with different lengths of operating time were adopted for bond coating. As a result, changes took place in its sur- face roughness and the surface micro-hardness. A thermal cycling test at 1 273 K×55 min and another at room temperature for 5 min were performed to study the effects of shot peening process on the thermal cycling lifetime of TBCs. It is found that a moderate shot peening process will be able to prolong the life time. The oxidation dynamic of the as-processed TBCs basically accords with the para- bolic rule, and the oxidation test also attests to the spallation between YSZ and thermal growth oxide (TGO) responsible mainly for the failure of TBCs.     

热障涂层中TGO的生长行为

采用等离子喷涂法在高温合金IC10上先后沉积粘结层为NiCrAlYSi,陶瓷层为Sc2O3-Y2O3-ZrO2的样品。样品在热循环炉中1100°恒温氧化,观察样品不同氧化时间的断面形貌,并绘制了样品的增重曲线,以此分析高温时TGO的生长过程。     

High-temperature oxidation behavior and analysis of impedance spectroscopy of 7YSZ thermal barrier coating prepared by plasma spray-physical vapor deposition

Quasi-columnar structure 7YSZ(yttria stabilized zirconia) thermal barrier coatings(TBCs) are prepared by plasma spray-physical vapor deposition(PS-PVD) onto pretreated and un-pretreated bond coating, respectively. An isothermal oxidation experiment of 7YSZ TBCs is carried out in the atmosphere of 950 °C in order to simulate the high-temperature oxidation process of engine blades. The isothermal oxidation process of 7YSZ thermal barrier coatings is investigated systematically by impedance spectroscopy. The electrochemical physical model and equivalent circuit of columnar 7YSZ coatings are established. Results show that the isothermal oxidation kinetic curve of columnar 7YSZ thermal barrier coatings appears to follow the parabolic law. A pretreatment of bond coating can reduce the growth rate of the thermally grown oxide(TGO) layer, restraining the initiation and propagation of microcracks between YSZ and TGO layers. The oxidation rate constants of 7YSZ coatings with pretreated and un-pretreated bond coating are 0.101×10~(-12) cm~2·s~(-1) and 0.115 × 10~(-13) cm~2 ·s~(-1), respectively. Impedance analysis shows that the content of oxygen vacancies decreases and the density increases after the TGO layer is oxidized for 150 h. In addition, shrinkage microcracks formed by sintering during the oxidation process is the main reason for an increase of the capacitance and a decrease of the resistance in the grain boundary of YSZ.     

双层氧化物生长下热障涂层的界面失效与应力演化

在长时高温服役环境下,热障涂层（TBCs）会在内部的陶瓷层（TC）和粘结层（BC）之间生成由Al2O3层和混合性氧化物层（MO）组成的双层热生长氧化物（TGO）。其中,后期生成的MO 由于其疏松多孔、脆性大等特点,极易造成涂层内微裂纹的形成和扩展,导致涂层的过早剥落。因此,依据双层TGO 生长的扩散—氧化模型,在考虑材料非线性变形行为的基础上,运用生死单元法模拟TBCs 内双层TGO 异向生长下涂层界面的失效与应力演化过程。结果表明：MO 的生长会大幅度提升涂层界面的拉伸应力水平,易导致MO/TC 界面在高温阶段波峰区域和冷却阶段斜坡中心区域发生破坏及失效;MO/TC 界面的失效会引起BC 层波峰处更高的拉伸应力,促进冷却阶段Al2O3/BC 界面从波峰向波谷处的破坏;MO/TC 界面失效后,hAl2 O3 /hMO 的增加会加速Al2O3/BC 界面的破坏。     

等离子-物理气相沉积硅/莫来石/硅酸镱环境障涂层的高温防护和耐热冲击性能研究

通过SiCf/SiC复合材料表面等离子喷涂(APS)硅黏结层和莫来石中间层,等离子-物理气相沉积(PS-PVD)制备硅酸镱面层,喷涂的整个环境障涂层体系组织致密,PS-PVD工艺制备的硅酸镱为层状结构,孔隙率＜1％.研究了 SiCf/SiC复合材料环境障涂层的抗静态氧化、循环氧化、水汽腐蚀和热冲击性能,发现复合材料表面...     

表面处理对热障涂层界面微结构的影响

采用真空电弧离子镀技术在单晶高温合金DD32上制备HY5金属粘结层,通过振动光饰、吹砂2种不同的表面处理方法改变粘结层表面状态,再在粘结层表面利用电子束物理气相沉积技术制备陶瓷层。研究了不同处理方法对粘结层表面状态的影响;测试了不同表面处理方法下制备的热障涂层的高温氧化性能并对比分析了它们的变化规律。此外,探讨了不同表面处理方法对界面元素成分及失效特征的影响。研究结果表明,通过表面处理可以去除粘结层表面较大的凸起,提高表面平整度,提高热障涂层抗氧化性能。与粗糙界面相比,光滑界面形成的TGO层均匀致密,Al含量高。经长时间的高温氧化后,粗糙界面的TGO层出现明显皱曲现象,陶瓷层开裂剥落。