带保载平面应变塑性诱发裂纹闭合效应

用黏塑性有限元法模拟含中心裂纹试件在等幅循环拉伸加载和保载作用下的裂纹扩展规律.试件采用涡轮盘材料Udimet720 Li(low inclusion)、恒温700℃和平面应变假设,通过逐步释放裂纹尖端节点约束来模拟裂纹扩展.计算了在应力比R=0,不同最大循环载荷、不同保载时间对平面应变下无量纲裂纹张开应力强度因子的影响.平面应变情况下,无量纲裂纹张开应力强度因子随最大载荷的变化而趋于分散,并随着裂纹的扩展,会存在先上升后下降并趋于一个稳定值的趋势;载荷相同时,保载时间的增加使裂纹张开应力强度因子增加.高温保载情况下,蠕变会影响裂纹扩展速率.      

弯曲载荷下薄壁结构疲劳裂纹扩展性能

对某飞机座舱盖侧型材与锁环连接部位的疲劳裂纹扩展性能进行了研究。该结构区别于常见薄壁结构的特征是承受较大的弯曲载荷,使得利用薄板I型裂纹扩展的常用方法进行寿命分析会产生较大的误差。为了研究弯曲载荷下薄壁结构的疲劳裂纹扩展性能,开展了带孔板和侧型材结构模拟件的疲劳裂纹扩展试验。通过有限元仿真分析,研究了弯曲载荷对裂尖应力强度因子的影响,提出了一种当量应力强度因子变程公式;对本文所涉及的2种类型受弯曲载荷作用的试件,裂纹扩展寿命预测结果与试验吻合较好。研究表明,在相同的名义应力和裂纹长度下,薄板受弯时裂纹应力强度因子、裂纹扩展速率远低于受拉的情况;结构受到弯曲载荷时,锁环对连接部位的应力有显著的抑制作用,可以减缓疲劳裂纹的扩展;此外,合理的结构设计能够增加关键部位受弯时的疲劳裂纹扩展寿命。     

航空发动机火焰筒疲劳裂纹扩展规律

利用合理的温度场、载荷谱,计算了火焰筒气膜唇边裂纹在扩展过程中最大应力强度因子Kmax的变化规律,利用Pearson经验公式预估了火焰筒热疲劳裂纹扩展速率,并给出了应力强度因子、裂纹扩展速率的初步分析结果.     

基于循环应变特征的疲劳-蠕变寿命预测方法

为研究非对称加载下疲劳-蠕变交互作用对粉末高温合金涡轮盘寿命的影响,开展了550 ℃时不同应力水平及保载时间下FGH96粉末高温合金的低周疲劳-蠕变试验,得到了材料的循环应变响应及疲劳-蠕变寿命随保载时间的变化规律。在此基础上,结合材料的循环软化特征,以循环应变范围作为损伤控制参量,将其与保载时间和动态循环次数相关联,提出了一种基于循环应变特征的疲劳-蠕变寿命预测方法。该模型综合考虑了载荷历程和保载时间对材料疲劳-蠕变损伤的影响,能够实现不同应力水平、不同保载时间下FGH96粉末高温合金疲劳-蠕变寿命预测以及消耗寿命的动态跟踪。通过与工程上常用的几种模型进行对比,发现新模型具有较高的预测精度,且预测结果分散性较小,寿命预测结果基本位于±2.5倍寿命分散带之内,预测标准差小于0.4。     

三维广布裂纹疲劳扩展分析

 飞机结构表面由于腐蚀、疲劳等原因存在三维广布裂纹,相邻裂纹在疲劳载荷作用下相互影响、相互促进,从而加速了结构破坏。为了探讨并求解三维广布裂纹结构的疲劳寿命,选取表面有两个半椭圆形表面裂纹的有限厚矩形板为计算模型,采用参数化有限元方法,求解裂纹前沿的应力强度因子、裂纹扩展方向和裂纹扩展增量,建立并应用应力强度因子变化历程,采用循环接循环损伤累积方法,对结构在疲劳载荷作用下的寿命进行了预测。预测结果为复杂环境中三维广布裂纹飞机结构的寿命评估提供了参考。     

预循环应力对材料断裂力学性能“锻炼”效应的影响

对服役多年的高速列车用7N01铝合金材料进行疲劳裂纹扩展速率试验,其对数坐标系中的疲劳裂纹扩展速率da/d N与应力强度因子ΔK的关系呈折线形式。与未服役材料对比,在裂纹扩展初期阶段,裂纹扩展速率降低。选取两种原始铝合金材料进行107次预循环应力作用后的疲劳裂纹扩展速率试验,研究低于疲劳极限的预循环应力对材料断裂力学性能的影响。结果表明:经预循环应力作用的材料,其da/d N与ΔK的关系曲线在裂纹扩展初期(对应于低应力强度因子阶段)均出现折转现象。对试验数据的回归分析表明:预循环应力的作用使得材料的断裂力学性能有所提高,预循环应力对材料产生"锻炼"效应。     

疲劳裂纹扩展过程中的CTOD相关参量分析

以2524铝合金与激光熔化沉积TC11钛合金为试验对象,开展了不同载荷条件下的疲劳裂纹扩展试验,采用数字图像相关方法(DIC)对裂纹尖端张开位移(CTOD)进行了测量,研究了CTOD、CTOD变程、CTOD塑性分量、CTOD滞回环面积等参量在疲劳裂纹扩展过程中的变化规律,分析了上述参量与疲劳裂纹扩展速率的相关性,提出了一种以CTOD滞回环面积为主控参量的疲劳裂纹扩展速率模型。研究结果表明,CTOD滞回环面积和CTOD塑性分量与疲劳裂纹扩展速率间均存在明确的关联关系,可有效地表征疲劳裂纹扩展中塑性行为的影响;采用CTOD滞回环面积表征疲劳裂纹扩展速率在恒幅与变幅载荷下均具有适用性,且受测量偶然误差的影响更小,在应用中具有一定优势。     

孔边角裂纹扩展特性分析

采用二维裂纹扩展分析方法研究含孔边角裂纹平板中疲劳裂纹扩展速率和寿命。该方法假设孔边角裂纹两个主方向上裂纹扩展主要取决于两方向裂纹尖端的应力强度因子。并采用裂纹闭合特性修正。预测在常幅拉伸疲劳载荷情况下２１２４Ｔ８５１铝合金板和３０ＣｒＭｎＳｉＮ１２Ａ合金钢板中孔边角裂纹扩展速率和寿命。理论计算和实验结果较吻合。     

钛合金扩散焊接头复合型疲劳裂纹扩展

设计并加工了TC4扩散焊接头紧凑拉伸剪切(CTS)试样。开展了不同加载角度下的Ⅰ-Ⅱ复合型疲劳裂纹扩展试验。试验结果发现:在加载角度小于45°时,裂纹均沿焊缝扩展至断裂,当加载角度达到45°以上时,裂纹开始出现沿与初始裂纹面呈一定角度的方向扩展至母材的情况。使用电子显微镜结合电位法获得了裂纹扩展a-N曲线。在此基础上,采用相互作用积分法计算复合型应力强度因子,以应变能释放率为参量对Ⅰ-Ⅱ复合型裂纹扩展过程进行了分析。考虑Ⅱ型裂纹所占权重引入复合比,并在此基础上建立了TC4扩散焊接头不同加载角度及载荷下Ⅰ-Ⅱ复合型疲劳裂纹扩展速率统一模型。      

疲劳应力变幅的断口反推研究

通过对18Cr2Ni4WA钢在不同应力比和不同载荷下的疲劳裂纹扩展速率试验,拟合得Paris关系式,然后对试验断口进行疲劳条带宽度S(微观裂纹扩展速率)测量,将疲劳条带宽度值代入拟合的Paris关系式中,反推计算断口试样的疲劳应力变幅.结果表明,疲劳条带宽度只在疲劳裂纹扩展的一定阶段与宏观裂纹扩展速率相等,选择该阶段的数据点进行疲劳应力变幅反推计算,相对误差在10%以下;数据点是否位于宏、微观裂纹扩展速率相等的阶段,可由S～yπa双对数座标S形曲线判定,并发现由于裂纹扩展速率的误差传递系数小于0.5,计算结果对裂纹扩展速率测量的相对误差不敏感.     

A new fatigue life prediction model considering the creep-fatigue interaction effect based on the Walker total strain equation

The performance of high-temperature components of aero-engines under the Creep-Fatigue Interaction (CFI) behavior gets more attention recently. In this research, the creep-fatigue tests of two superalloys of Powder Metallurgy (PM) FGH96 and direct aging GH4169 were performed at 650 °C with different types of dwell, and the fracture morphology of FGH96 specimens was observed by Scanning Electron Microscopy (SEM) to analyze the creep-fatigue fracture feature and crack initiation. Additionally, according to phenomenology, the effect of dwell was introduced to develop a new uniaxial fatigue life prediction model based on the total strain equation, which has capability to take dwell time and load ratio into account together. The equations were utilized to model the test data of PM FGH96 and GH4169, together with data of another superalloy PM FGH95 conducted previously. A prominent prediction ability of the model in creep-fatigue life prediction of different superalloys has been manifested. Most data points of test data and estimated data are located within two times scatter band, which is ideal in engineering.     

直接时效GH4169高温合金疲劳裂纹扩展性能试验

对直接时效GH 4169高温合金的疲劳裂纹扩展性能进行了试验研究。分别研究了厚度、温度、应力比等因素对直接时效GH 4169高温合金疲劳裂纹扩展性能的影响。结果表明,在410 mm的厚度范围内,厚度对直接时效GH 4169高温合金疲劳裂纹扩展性能几乎没有影响,但厚度为2 mm且应力比为0.1时其裂纹扩展速率稍有下降;应力比对直接时效GH 4169高温合金疲劳裂纹扩展的影响随着应力比的提高逐渐减小;温度的提高对直接时效GH 4169的裂纹扩展速率有明显的加速作用,但是随着应力强度因子范围的增加,其影响逐渐减小,氧化作用是加速其裂纹扩展的主要机理。      

多孔多裂纹平板的疲劳裂纹扩展试验与分析方法

飞机结构广布疲劳损伤是目前大型客机损伤容限设计与分析的难点。通过试验研究了典型多孔多裂纹2024-T3铝合金平板的裂纹扩展行为。试验结果表明：相邻孔边裂纹之间的相互干扰明显降低了共线多裂纹平板的疲劳裂纹扩展寿命。就本文研究的典型多孔板,所有孔边都出现了等长裂纹这一极端情况,其裂纹扩展寿命是单孔平板孔边裂纹扩展寿命的10%左右。本文采用Eshelby夹杂理论和权函数法给出了典型多孔多裂纹问题的应力强度因子近似解析解,并结合Paris裂纹扩展公式预测疲劳裂纹扩展寿命。与采用有限元法获得应力强度因子并预测多孔多裂纹板的疲劳裂纹扩展寿命进行对比,对比结果表明：采用解析解和有限元解获得的应力强度因子预测的疲劳裂纹扩展寿命与试验结果吻合良好;相比于有限元法,本文的应力强度因子解法简单、高效,将有助于飞机结构多位置损伤（MSD）的疲劳裂纹扩展寿命预测分析。     

EFFECT OF OVERLOAD ON CRACK GROWTH IN FIBER REINFORCED METAL LAMINATES

Ｆｉｂｅｒｒｅｉｎｆｏｒｃｅｄｍｅｔａｌｌａｍｉｎａｔｅｓ（ＦＲＭＬｓ）ａｒｅａｇｒｏｕｐｏｆｍａｔｅｒｉａｌｓｂｙｂｏｎｄｉｎｇｔｈｉｎｍｅｔａｌｓｈｅｅｔｓｗｉｔｈｆｉｂｅｒｃｏｍｐｏｓｉｔｅｓ［１３］,ｔｙｐｉｃａｌｙｗｉｔｈ２／１ｌａｙｕｐ...     

8090铝锂合金疲劳短裂纹扩展行为研究

 研究了8090铝锂合金二维短裂纹的扩展行为,发现了短裂纹扩展抗力明显低于长裂纹,且随裂纹尺寸不同而异,其原因是裂纹闭合效应随裂纹尺寸变化。应用有效应力强度因子幅值可统一各种尺寸短裂纹乃至长裂纹的扩展行为。     

TC4-DT焊接接头Ⅰ-Ⅱ复合型疲劳裂纹扩展实验及模拟研究

拉剪复合载荷作用下,构件中的裂纹呈现复杂的Ⅰ-Ⅱ复合型扩展模式,研究其扩展规律对准确评估构件疲劳寿命具有重要意义。针对TC4-DT钛合金电子束焊接头Ⅰ-Ⅱ复合型疲劳裂纹扩展规律开展研究,设计并加工紧凑拉伸剪切(CTS)试样,通过开展不同加载角度下接头试样的疲劳裂纹扩展实验,得到接头Ⅰ-Ⅱ复合型裂纹的a-N曲线及疲劳裂纹扩展路径。在上述基础上引入Ⅰ-Ⅱ复合型等效应力强度因子并结合Paris公式建立TC4-DT电子束焊接头Ⅰ-Ⅱ复合型疲劳裂纹扩展速率方程。采用扩展有限元法(XFEM)对复合型疲劳裂纹扩展过程进行数值模拟研究,得到不同加载角度下的扩展规律,并与实验结果进行比较。结果表明:不同加载角度下Ⅰ-Ⅱ复合型疲劳裂纹开裂角模拟值与实验结果误差均在10%以内,并且扩展路径均与实验结果吻合;XFEM能够有效预测复合型疲劳裂纹扩展路径。     

考虑裂纹形状变化的TC4钛合金振动疲劳裂纹扩展寿命预测

对TC4板材试件进行振动疲劳裂纹扩展试验,测得裂纹扩展寿命与裂纹长度之间的关系.使用超景深显微镜对裂纹形状进行观测和分析,拟合裂纹形状参数.将拟合表达式应用于应力强度因子幅值的计算中,并对裂纹扩展寿命进行预测.结果显示:裂纹形状参数对预测结果影响较大.当该参数取定值时,预测结果与试验结果误差较大.而所拟合的拟合表达式可以简单、准确地预测裂纹扩展寿命.      

FGH96涡轮盘低循环疲劳寿命分析技术与试验

分析FGH96涡轮盘的尺寸效应,分析了分别适合于FGH96亚尺寸盘和全尺寸盘的低循环疲劳寿命预测方法.成功设计了FGH96亚尺寸盘、全尺寸裂纹扩展盘试验件;通过低循环疲劳试验,展现了两种不同的低循环疲劳失效机理,验证了提出的低循环疲劳寿命预测方法;通过裂纹扩展试验,获得了FGH96全尺寸轮盘的裂纹扩展特性,揭示了FGH96全尺寸涡轮盘与紧凑拉伸试样裂纹扩展特性具有显著差别的客观规律;获得FGH96全尺寸涡轮盘580℃损伤容限值,明确某发动机高压涡轮盘损伤容限水平.      

考虑应力比的疲劳裂纹扩展概率模型

考虑到应力比对疲劳裂纹扩展速率的影响及裂纹扩展的分散性,在Paris公式基础上,提出了一种考虑应力比的疲劳裂纹扩展概率模型;运用非线性函数线性化原理给出概率模型参数的求解方法;通过该概率模型和曲面,可从宏观上把握应力比对裂纹扩展的影响规律及得到任意应力比下的概率疲劳裂纹扩展速率曲线;对30CrMnSiNi2A钢试验数据的处理及分析验证了该模型的有效性和实用性.