冷却速率对TC21合金相变行为的影响

采用末端淬火法研究了TC21合金自β相区冷却后冷却速率对合金相变和显微组织的影响,对取自末端淬火试样的不同区域试样进行了OM、XRD、TEM及显微硬度分析。结果表明:冷却速率大于122℃/s时,β相转变形成正交马氏体α″,冷速介于122℃/s和3℃/s之间时,发生块状转变,冷速继续降低,相变由扩散控制,形成两种不同形貌的魏氏体α片层:较平滑的α片层和较曲折的α片层;随冷却速率的降低,合金的显微硬度先增大后降低,冷却速率小于8℃/s后,显微硬度迅速降低。     

宽变冷速对定向凝固合金枝晶偏析的影响

利用多种定向凝固技术,研究了冷却速率在10~(-2)～10~2K/s范围内变化时对定向凝固钻基高温合金枝晶偏析的影响。结果表明:增大冷却速率可有效抑制枝晶偏析,对易偏析元素其效果更明显;冷却速率的增大细化了凝固组织的一次间距、加剧了溶质的非平衡分凝是抑制偏析的主要原因。     

一种超高强铝合金的熔铸工艺研究

详细研究了一种超高强铝合金的熔铸工艺,对铸锭的杂质控制、合金熔体的保护、晶粒细化以及铸造工艺参数的配合等多方面进行了研究,尤其是针对该合金在连铸过程中易出现的热裂问题进行了全面研究,提出了控制铸锭开裂的工艺方法.结果表明,该工艺方法可以进行φ290mm及φ308mm锭的铸造,成品率可在90%以上.     

单面射流冲击淬火参数对7050铝合金厚板冷却的影响

研究了喷嘴直径(D)、相邻喷嘴距离(L)和喷射压力(P)对驻点区和紊流区换热的影响.结果表明:在高压(500kPa)下,紊流区心部换热效果比驻点区心部强;当喷嘴直径和喷射压力一定,相邻喷嘴距离对厚板冷却有影响,距离越小,相邻涡对互相干扰越大,紊流区冷却强度加大;当L/D=8～14时,从470℃冷至300℃的平均冷却速率...     

摆盘流动与换热性能数值仿真

针对受燃烧室出口高温燃气冲刷的摆盘装置的冷却水回路,建立二维、三维物理仿真模型,模拟了冷却水在内部流道的 流动与换热过程,考察了冷却水进口压力、冷却水流量对流阻和换热性能的影响.结果表明:①摆盘冷却水进口压力由2.3×105Pa提高到8.3×105Pa,摆盘壁温变化微小,结构1壁温升高5K,结构2壁温升高7K;②冷却水进口速度由0.5m/s提高到5.3m/s,结构1壁温降低约120K,结构2壁温降低约100K,冷却效果明显;③结构2通过缩小流道的流通面积,能在更小的冷却水流量的工况下得到更好的换热效果.      

扇形喷嘴燃油浓度场试验研究

 在常压和气流速度 Va=5 0～ 90 m/s、气流温度 T=2 83～ 673K、油压 Pf=0 .2～ 0 .8MPa,下游距离 x=1 0 0～ 1 90 mm的条件下 ,对某扇形喷嘴下游燃油浓度分布的影响进行了试验研究。试验表明 ,扇形喷嘴油雾场的纵向分布呈扇形 ,横向分布与直流式喷嘴侧喷类似。当气流速度减小、气温降低、油压升高或下游距离增大时 ,都会引起燃油分布范围及穿透深度增加     

复合材料主动冷却薄壁燃烧室设计分析

通过建立流固耦合传热模型,对不同尺寸冷却通道的主动冷却薄壁燃烧室结构瞬态传热特性进行数值模拟,给出了主动冷却燃烧室的瞬态温度场分布及其演化.再采用有限元法计算燃烧室的热应力和应变,从而揭示了冷却通道几何参数及内部煤油体积流量对燃烧室薄壁结构最高温度和热应力的影响规律.计算结果表明:在充分发挥煤油冷却效果前提下,冷却通道距离燃烧室内壁距离越近,所需煤油体积流量越大,而燃烧室结构热应力在10s左右达到最大值,设计时应着重考虑这段时间内的材料性能.      

超燃冲压发动机壁面热量的利用潜力分析

在高马赫数飞行下,用燃料冷却超燃冲压发动机壁面的冷却需求量大于发动机燃烧量。为了降低燃料的冷却量以及实现燃料冷却量和燃烧量的匹配,采用可用能分析法对超燃冲压发动机壁面热量的利用潜力进行分析。发动机壁面热量特性及燃料的冷却特性决定可用能大小。根据发动机壁面温度分布、热流密度分布及燃料的冷却过程温度分布计算可用能。该方法得出:在壁面最高温度为1200K时,传入壁面的热量为554.4k W,其中理论可用能为331.6k W。没有利用其热量实现热量转换时需要的燃料冷却流量为0.616kg/s,最大限度利用热量实现能量转换输出可用功时只需要燃料冷却流量为0.2476kg/s,降低了燃料的冷却需求量。     

铸造铝合金热分析技术研究

介绍了铸造铝合金热分析原理,主要研究了铸造铝合金晶粒度和共晶组织变质的热分析特征,选择和测定了冷却曲线上的ΔTl,tR和ΔTE,te两组特征点,提出了铸造铝合金晶粒细化和共晶硅变质程度的判据,为热分析法铸造铝合金质量控制提供了依据.     

可压缩算法在燃油冷却数值研究中的应用

为深入研究超燃冲压发动机的燃油主动冷却过程,在可压缩算法框架下,引入预处理技术、低耗散数值离散格式、一般流体状态方程、高压物性模型、燃油裂解模型等,发展了一套适用于求解一般流体低速可压缩问题的数值模拟方法。利用电加热管试验对数值方法进行了验证,并定量研究了PR-3燃油的冷却需求量及平板面板冷却槽道布置的影响。结果表明,数值结果与试验符合很好,证明当前数值方法在燃油冷却数值模拟中是准确有效的。针对350mm×90mm×6mm的平板面板冷却过程,需要约10g/s的燃油可确保1WM/m2热流下的防热安全。槽道布置对温度场影响明显,两侧进油方式比单侧进油的最大温差低约150K,均温性更好,更有利于降低结构热应力。     

短纤维增强铝硅合金中共晶硅形貌的SEM观察

利用挤压铸造制备了氧化铝短纤维增强铝硅合金复合材料，在sEM上观察了复合材料中的共晶硅形貌。结果表明，复合材料中的氧化铝短纤维可作为硅相非自发形核的衬底，并且在铝硅共晶体的共生生长过程中，可触发孪晶，导致纤维附近的共晶硅呈变质形态。     

Al-Si合金几种变质剂变质作用差异的探讨

Al-Si合金中几种常用变质剂的变质效果明显不同。从不同角度对各种元素的变质作用机理进行了探讨,但对于这些元素在变质效果上的差异尚未得到完满的解释。作者前期的工作采用XPS和AES表面分析技术检测了Sr在Si相的特定晶面的吸附性。本文将运用同样的实验方法,分别对Na、RE、Sb等变质剂作相应的考察,并对这些变质剂变质作用的差异进行探讨。     

铸造凝固冷速对原位自生（TiW）C／Fe复合材料组织的影响

研究了不同的铸造凝固冷速对原位自生10vol%(TiW)C/Fe复合材料显微组织的影响。结果表明,在原位合成的10vol%(TiW)C/Fe复合材料中,(TiW)C相是唯一的第二相,均匀、弥散分布于基体中,其形态基本上呈块状,条状较少。在块状(TiW)C相中,Ti和W元素的分布是不均匀的,芯部富Ti,边缘富W。当冷速较快时,形成的第二相颗粒趋于等轴状,条状共晶组织消失,有利于基体耐磨性的提高;当冷速较慢时,第二相颗粒数量多,尺寸小,且随冷速的降低在该复合材料中形成了大量的共晶组织。适当提高冷却速度,有利于获得较理想的复合材料显微组织。     

利用液晶测量吹风比对尾缘半劈缝换热特性的影响(英文)

This article deals with the effects of a blowing ratio measured with narrowband liquid crystal in transonic experiments on the heat transfer characteristics of trailing edge cutback. The experimental results are compared and contrasted in terms of available data for traditional experiments with thermocouples. It is concluded that the blowing ratio exerts rather significant effects on film cooling effectiveness distribution of the rib center line. As the blowing ratio decreases, similar to the cooling effectiveness distribution curve of the slot center line, that of the rib center line makes a clockwise rotation about the end. When the blowing ratio increases, the regular film cooling effectiveness curve of the surface becomes rather smooth. On the whole measuring surface, the most intensive heat transfer occurs at the extended borderline of the slot and the rib, neither at the rib center line nor at the slot center line. The experimental results of cooling effectiveness measured with thermocouples are lower than those with liquid crystal. In addition, the transient experiments using narrowband liquid crystal can eliminate the higher errors of Nusselt numbers in measurements with thermocouples at the slot outlet.     

低镍奥氏体不锈钢定向凝固组织CAFE法模拟

通过对ProCAST&CAFE软件进行二次开发建立凝固过程动态边界条件,模拟低镍奥氏体不锈钢定向凝固过程中的温度场和固相分数,并探讨抽拉速率对凝固微观组织的影响。结果表明,随着抽拉速率的增大,等温线变密,糊状区变窄;铸件一次枝晶臂逐渐细化,边缘侧向散热逐渐远小于中心纵向散热造成一次枝晶轴向偏差度逐渐减小,晶粒择优取向效果提高。与此同时,模拟结果与实验结果吻合较好,模拟计算形核、生长及取向过程较为合理。     

Gd-Tb二元稀土基非晶合金（Gd-Tb）-Al-Co的非晶形成能力及热稳定性

采用铜模铸造法制备Gd-Tb二元稀土基非晶合金(Gd-Tb)-Al-Co。确定(Gd-Tb)-Al-Co合金系的非晶形成区域及非晶形成能力。利用差示扫描量热仪对非晶合金的热稳定性以及合金的熔化和凝固过程进行研究。结果表明,Gd-Tb二元稀土基合金(Gd-Tb)-Al-Co的非晶形成能力远大于单元稀土基合金Gd-Al-Co或Tb-Al-Co的非晶形成能力。在(Gd-Tb)-Al-Co合金中,高非晶形成能力合金位于共晶点附近,非晶形成能力最好的合金(Gd0.5Tb0.5)55Al25Co20位于陡峭的液相面一侧,其临界直径(dc)可以达到5mm。与Gd55Al25Co20和Tb55Al25Co20合金相比,原子尺寸相似的Gd和Tb两个稀土元素降低相应合金的凝固温度,提高液相的稳定性,从而提高合金的非晶形成能力。     

狭小空间内气膜孔流量系数的数值模拟

针对多层层板冷却、双层壁冷却等冷却技术,利用数值模拟分析了这些冷却结构形成的狭小冷却通道中,气膜孔附近的流动特性,重点研究了气膜孔流量系数C_{d随吹风比M(0.5～2.0)、气膜孔雷诺数Re(5000～10000)以及冷却通道高度H和气膜孔直径D之比H/D(0.33～1.0)等参数的变化规律.数值计算中湍流模型为Realizable k-ε模型,近壁处采用非平衡壁面函数,利用SIMPLE算法和二阶迎风格式进行离散求解.计算结果表明:气膜孔流量系数随吹风比的增大而增大,在吹风比M小于1时,影响尤为明显.研究中同时发现在相同吹风比的条件下,Cd随着气膜孔雷诺数的增大而减小,但变化的幅度不大;在相同的气膜孔雷诺数下,Cd随着H/D的减小而降低,特别是当H/D小于0.75时,随着流体在进入气膜孔前逐步受到限制,Cd随着H/D的减小而快速降低.}      

吸入式空冷汽轮发电机气体运动流场分析及应用

为了提高空冷汽轮发电机的冷却效果,改变原压入式空冷汽轮发电机通风方式,空气由定子风道和转子风道进口进入,由吸入式风扇排出,消除了原压入式汽轮发电机由于风扇进风而带来的风道进口温度升高以及转子风道的热风进入定子风道造成定子风道进风口温度增加,改善了冷却效果。采用模型试验和数值模拟方法对吸入式空冷汽轮发电机风道气体运动流场进行了分析,结果表明：吸入式空冷汽轮发电机转子风道进口风速一般为10.0~90.0m/s,和压入式空冷汽轮发电机转子风道进口风速基本相同;距汽端近1.0m范围内,定子风道风速一般为8.0~18.0m/s,距汽端1.5~3.0m范围内,定子风道中风速仅为3.0~5.0m/s,为了使定子得到均匀冷却,将前15个风道间距增加至80.0mm,后25个风道间距减小至45.0mm,可在总风道数目基本不变的情况下改善冷却效果。     

冲击+逆向对流+气膜冷却传热特性的研究

为了研究火焰筒壁面冲击+逆向对流+气膜复合冷却方式的传热特性, 设计了6种不同几何结构的实验件, 搭建了实验台, 采用红外热像仪对其传热特性进行了研究.结果表明, 冷却效率随吹风比的增大而增大;在气膜出口与冲击位置之间, 气膜冷却效率沿主流方向不断增加, 在相同的冷却壁面处, 冷却效率随冲击位置距气膜出口的增加而减小;越过冲击位置, 冷却效率随壁面位置的增加而减小.在冷却壁面的任一位置, 冷却效果随冲击间距的减小而增大.      

典型尖楔结构燃气流热试验工况确定方法

在传统冷壁热流模拟方法的基础上,进一步提出以热壁温度及热流密度的时序变化曲线为控制目标的燃气流热试验工况确定方法,即利用壁温控制目标与实测值的偏差对热壁热流控制目标做一定修正,以尽可能消除和弥补前期试验误差,同时利用300K冷壁边界热流密度数据库插值迭代方法,快速确定一定气动热模拟所需燃气流温度,解决了沿飞行轨迹瞬态热试验技术难题之一。利用CFD数值模拟方法,建立了典型尖楔结构高/中温双路燃气流组合热试验300K冷壁边界热流密度数据库,并针对典型尖楔结构沿某飞行轨迹9个典型状态气动热模拟需求,确定相应双路燃气流热模拟参数。相关数值计算结果显示,驻点区域热流密度平均模拟偏差为4.5%,平板区热流密度平均模拟偏差为4.6%,两者最大模拟偏差均不大于8%,满足工程试验精度要求。同时,瞬态热分析结果显示第45s时,距驻点1mm处最大温度梯度达到21K/mm,距驻点10.1mm处最大温度梯度达到18K/mm,满足气动热大温度梯度效应需求。