 采用高能激光束作为定向凝固的热源,研究了镍基合金在超高温度梯度（1.0×104K/cm）定向凝固下的组织结构特征。在定向凝固组织中得到了平均一次枝晶间距仅为10.6μm的细枝晶和完全无侧向分枝的“超细胞晶”.对合金元素在不同组织中偏析行为的分析表明：传统的定向凝固组织中存在严重的微观偏析,而激光超高温度梯度定向凝固组织中,元素的微观偏析大大改善甚至完全消除。     

激光近形制造镍基合金的显微组织及其力学性能

根据相图确定了适宜于激光烧结的镍合金粉末的组成--84Ni14.4Cu1.6Sn.用气雾化工艺制备了该粉末,并进行预处理,烧结出镍基合金的薄壁墙和厚壁墙零件.研究了工艺参数对薄壁零件显微硬度的影响.经拉伸试验、金相分析和SEM分析,研究了厚壁墙的显微组织和部分力学性能.     

网状电极形状参数对高温镍基合金电解加工的影响

为研究网状电极形状对GH4169高温镍基合金电解加工的影响规律,采用电极\"抬刀+摇动\"的方式,进行了0. 5、0. 8和1. 0 mm孔径的平面网状电极对比实验以及曲面网状电极和平面网状电极对比实验。结果表明,当孔径为0. 5 mm时,不足以将加工屑有效排除,加工不能持续进行;随着电极孔径的增大,加工稳定性增强,速度增大,但精度降低。采用曲面网状电极加工时,由于摇动平面与所需加工面不平行,造成工件表面不平整。在实际加工中,应当根据对稳定性、速度以及精度的具体要求合理选择网状电极形状参数。     

涂层硬质合金刀具加工镍基合金的应用

本文在对镍基合金进行系统车削实验基础上,研究了多种先进硬质合金刀片的切削性能。并对涂层硬质合金刀片独特的优良性能进行了论述。文中从抗磨料磨损、抗扩散磨损及抗氧化磨损几方面,对涂层刀具的切削机理进行了分析研究。     

聚焦透镜和加工环境对飞秒激光加工镍基合金的影响

针对飞秒激光加工镍基合金材料,研究了4种数值孔径的聚焦透镜和3种加工环境(空气、真空和氩气)对飞秒激光加工效率和重铸层的影响。实验结果表明:聚焦透镜数值孔径越大,聚焦后激光能量密度越大,加工效率越高,而焦深越小,可加工材料厚度越小。在空气、真空和氩气3种加工环境下,镍基合金飞秒激光加工的重铸层厚度随着脉冲个数的变化规律相似,在相同脉冲个数下,3种加工环境中加工深度差距不大。     

镍基合金激光熔覆MCrAlY涂层基体裂纹的成因与控制

在分析激光熔覆涂层基体裂纹形成机理的基础上,针对采用激光熔覆技术在镍基合金基体上制备MCrAlY涂层存在基体裂纹的问题,提出了缓冷处理的止裂措施,研究了将熔覆后的涂层置于300℃下保温30min随炉缓冷和置于已预热至300℃的保温箱中随箱缓冷两种缓冷工艺对基体裂纹的控制行为.结果表明:镍基合金激光熔覆MCrAlY涂层基体裂纹主要是由于熔覆过程中的快速冷却所致;两种缓冷工艺均能有效地避免基体裂纹的产生,但保温随炉缓冷处理会引起熔覆层组织粗大、枝品特征明显等不良影响,而随箱缓冷处理涂层对熔覆层组织并未产生不良影响.     

改善激光加工Ni3Al基合金小孔质量的研究

介绍了针对金属间化合物-Ni3Al基铸造高温合金,提高激光加工小孔微观质量研究的最新进展,介绍了150～550 ns窄脉冲声光调Q脉冲列工作模式的YAG激光加工Ni3Al材料的特点及小孔的微观质量状况并与自由振荡YAG激光加工进行了比较;介绍了激光加工Ni3Al材料小孔孔壁再铸层后续去除的新方法--电化学腐蚀的工作原理、处理效果、性能分析等.     

涡轮叶片气膜孔的纳秒-飞秒双波段激光加工

针对航空发动机中涡轮叶片气膜孔的复杂加工要求,提出并建立了一套基于纳秒–飞秒双波段激光加工的方法与系统.使用三维扫描仪对涡轮叶片气膜孔进行空间坐标获取,对气膜孔的实际加工坐标进行了误差校正,实现了气膜孔的高精度定位.综合利用532nm纳秒激光高效率与400nm飞秒激光高精度的特点,在不锈钢涡轮叶片上实现了81个气膜孔的...     

能量密度对水工质激光推进性能的影响

当辐照激光能量密度不是很高时,在分析水工质激光推进基本物理过程的基础上,只考虑汽化过程对冲量形成过程的贡献,用一维理论模型研究了辐照激光能量密度对冲量耦合系数、比冲、能量转化效率等推进性能参数的影响规律。结果表明,随着辐照激光能量密度的增加,存在一个获得最大冲量耦合系数的最优能量密度;比冲随着能量密度的增加而变大;对于透射率一定的工质而言,随着能量密度增大,能量转化效率趋于一个恒定值。这一理论研究结果对下一步的实验研究工作具有较好的指导意义。     

激光快速成形镍基高温合金研究

在单道熔覆及薄壁墙试样制备的基础上 ,大致确定出Rene′95激光快速成形时的工艺参数和每层沉积高度 ,根据此高度对零件的CAD模型进行分层切片处理 ,生成二维平面信息 ,经过数据后处理并加入加工参数 ,生成数控信息输入成形系统 ,控制成形系统的沉积过程顺序完成各层的成形制造 ,直至加工出与CAD模型相一致的具有复杂外形的致密的金属零件。成形所用激光功率 16 0 0W ,扫描速度 3mm/s ,送粉速率 6 2g/min ,载气流量 0 3m3 /h ,所制零件总高 112mm(共沉积 380层 ) ,壁厚约 3mm ,每层沉积高度为 0 3mm ,零件具有良好的外形和尺寸精度。结果表明 :激光快速成形Rene′95镍基合金组织致密 ,成分均匀 ,沿成型高度方向具有定向凝固组织特征 ,具有较高的力学性能 但由于成型时存在很高的残余应力 ,容易导致开裂 ,通过基板预热可减缓应力。     

保温时间对K452高温合金钎焊接头组织与性能的影响

采用钴基钎料及镍基合金粉料,分别在1170℃保温10min、60min和120min的钎焊工艺下,对K452镍基铸造高温合金进行真空钎焊实验,通过扫描电镜和能谱分析仪进行了接头显微组织观察与物相分析,并测试钎焊接头的高温力学性能。结果表明:在保温60min的工艺规范下,界面实现较好的结合,钎缝内部孔洞缺陷较少,钎缝组织均匀,有利于钎焊接头性能的提高;在更长的保温时间120min下,钎缝内部又有蚀孔缺陷形成,且较多的白色块状化合物在合金粉颗粒间聚集长大,但界面结合良好,钎焊接头性能较高,900℃抗拉强度达到400MPa,900℃/100MPa持久寿命为141h55min。     

激光熔覆直接制造致密金属零件裂纹问题的分析

利用激光熔覆方法制造致密金属零件时,从熔覆工艺、熔覆材料、基体因素等方面分析裂纹产生的原因,并提出一些解决熔覆层开裂问题的新的设想。     

Modeling and Experimental Investigation of Laser Drilling with Jet Electrochemical Machining

As two kinds of defects, recast layers and spatters, commonly accompanied by laser-drilled holes always prevent the laser drilling technique from extending its applications in aerospace and aircraft industries, therefore, a novel hybrid process incorporating laser drilling with jet electrochemical machining (JECM-LD) has been developed to solve these problems as well as improve the overall quality of laser-drilled holes. It is executed by directing an electrolyte jet coaxially aligned with a laser beam onto the workpiece surface. During the process, the electrolyte jet produces electrochemical reaction with the surface material, effective cooling of it and carries away the process scraps. A two-dimensional mathematical model is proposed to describe the shape of the holes machined by JECM-LD. The model is verified through comparison between the results from simulation and those from experiments conducted on the test pieces made of 321 stainless steel 0.5 mm thick processed by the pulsed Nd:YAG laser at second harmonic wavelength. An examination of the experimental results under an optical microscope discovers that, by contrast with the laser drilling in air, the JECM-LD has effectively removed the recast layers and spatters, but its efficiency dropped by about 30%.     

固溶处理定向凝固高温合金DZ8的组织与力学性能

观察了1260℃与1240℃固溶温度热处理后DZ8合金的显微组织,比较了两者的拉伸与持久性能.结果表明:采用1260℃固溶温度热处理,DZ8合金存在少于1％的γ+γ'共晶相,但富Hf相发生初熔;采用1240℃固溶温度热处理,合金未发现初熔但仍存在12％左右的γ+γ'共晶相.DZ8合金分别采用1260℃与1240℃固溶温度热处理后,室温、700℃与980℃拉伸性能以及980℃/205 MPa持久性能相当,但采用1260℃固溶温度热处理的D28合金其760℃/725 MPa持久性能较采用1240℃固溶温度热处理的有所下降.     

长期时效对低膨胀高温合金GH783组织与性能的影响

研究了750℃长期时效对GH783组织与性能的影响.测试了合金的力学性能,并采用光学显微镜和扫描电镜对合金的组织进行了分析.结果表明:GH783合金在750℃长期时效过程中,随着时效时间的延长,γ'相尺寸长大比较明显;β相析出增多;合金的强度和持久寿命有所下降,而延伸率和断面收缩率有所提高.     

在DD3单晶上进行FGH95粉末激光多层涂覆:单晶涂层组织形式规律研究

利用高温合金 FGH95粉末在 DD3单晶的不同晶面上进行激光多层涂覆实验 ,深入研究了涂覆层中凝固显微组织的生长规律。研究表明基材的晶体取向和局部凝固条件对涂层中的凝固显微组织有很大的影响。当单晶基材择优晶向与热流方向夹角小于 30°时 ,可以得到从基材上外延生长的单晶 ,涂层内二次臂退化 ,枝晶一次间距为 10～ 2 0 μm;当实验所在的单晶基材的择优晶向与热流的方向夹角大于 30°时 ,涂层中晶体取向偏离基材的取向 ,并出现多晶。即便当实验在同一个择优晶面上进行时 ,局部凝固条件不同 ,涂层内的凝固显微组织也有很大的差别。二次臂退化 ,一次臂间距大约为 10～ 2 0 μm。进一步的研究表明 ,涂层中主要组成相为枝晶干上分布的基体相 γ和沉淀硬化相 γ′以及枝晶间的 γ+γ′花状共晶和少量碳化物 ,γ′相主要为具有良好强化效果的细小立方体 ,尺度约为 0 .1μm     

冷却速率、保温时间对DD3单晶合金TLP连接接头组织和性能的影响

对DD3单晶合金进行1250℃保温不同时间的TLP扩散连接研究。降温过程采取了随炉冷却和充氩快冷两种方式,随后对接头进行了870℃/32h/空冷的时效处理。分析了不同规范下的焊缝及母材的组织,同时测定了接头的980℃持久性能。结果发现:炉冷并时效处理试样的焊缝及母材中的γ'相的尺寸随着保温时间增加而增加,且形状趋于不规则。而充氩冷却并时效处理试样的焊缝及母材中的γ'相的尺寸和形状基本一致,随保温时间的增加没有明显变化,立方化较好。低的冷却速率使焊缝和母材中的γ'相粗化从而降低了接头和母材的性能,而高的冷却速率促使焊缝及母材中形成细小立方化的γ'相,不仅使接头性能明显提高,同时母材性能也没有降低。     

变形温度及变形量对挤压态FGH96合金晶粒异常长大的影响

基于楔形试样等温锻造试验,采用Deform-3D模拟软件,模拟确定了楔形试样中不同位置的变形量,研究了不同变形温度和不同变形量对挤压态FGH96合金晶粒异常长大的影响。结果表明：在压下速率0.04 mm/s的平模镦粗试验条件下,挤压态 FGH96合金出晶粒异常长大的临界变形温度为1100℃,临界变形量为2%;1000~1070℃锻造变形时,合金不易发生晶粒异常长大,但也有“临界变形量”特征,变形量5%~10%区域晶粒平均直径最大;选择15%及以上的变形量,可以避免晶粒异常长大,并获得均匀细小的晶粒组织。