Tensile properties of a composite–metal single-lap hybrid bonded/bolted joint

Hybrid bonded/bolted (HBB) joint has been widely used in engineering practice because it can overcome the potential weakness of pure bonded and pure bolted joints. However, studies on HBB joint are still at the initial stage. In this paper, tensile properties of a composite–metal single-lap HBB joint was investigated experimentally. And a detailed finite element model (FEM) was established to simulate the tensile behavior of the joint. The model was verified by the experimental results. Then the damage propagation and load transfer mechanism were explored based on the FEM. The results show that the HBB joint can provide multi-load transmission paths and resist damage propagation in the adhesive. The HBB joint has higher strength and energy absorption capacity than the pure bonded joint. And the HBB joint has greater initial damage load and tensile stiffness than pure bolted joint. Adhesive fillets can obviously improve the tensile performances of the HBB joint. Lateral stiffness of the joint boundary and testing machine show obvious effects on tensile performances of single-lap hybrid joints.     

超声冲击对TA15 钛合金焊接接头的影响

研究了TA15钛合金氩弧焊焊接接头超声冲击前后的组织及力学性能,并对接头拉伸断口进行了观察。结果表明,焊接后焊缝区和热影响区的组织与母材的组织差别很大,表现为魏氏组织特征;超声冲击前后母材和接头的组织均变化不大。冲击处理使焊缝区和母材区的强度和伸长率均有所增加。冲击前后的焊缝及母材的室温拉伸断口均属于韧窝型断口。冲击后接头的表面和断面显微硬度均得到了提高。     

酚醛/环氧过渡层固化特性及复合材料性能

为满足固体火箭发动机复合材料壳体的结构功能一体化要求,研究了两种树脂的过渡层配方、工艺及性能,重点研究了在酚醛树脂B30、环氧树脂TDE-85和固化剂甲基六氢苯酐（MHHPA）体系中,三者不同质量分数下的性能特点,采用了数显旋转黏度计和数显恒温水浴锅对树脂黏度测量,使用差示扫描量热仪（DSC）对不同质量分数的树脂进行热分析,求解多相体系反应机理的动力学参数,验证过渡层树脂固化工艺及性能,并与未使用过渡层的树脂配方进行性能对比。结果表明:过渡层体系中,最先反应的是B30和固化剂MHHPA,最后是B30的自固化;环氧树脂TDE-85的力学性能与酚醛树脂B30耐烧蚀性能满足结构层与功能层性能需求;与未使用过渡层的树脂相比,使用过渡层的树脂耐烧蚀性变化不大,但是弯曲强度提高了67.8%,拉伸强度提高了56.1%;与未使用过渡层的复合材料相比,使用过渡层的复合材料层间剪切强度提高了94.9%,但耐烧蚀性变化不大。综上所述,该过渡层可以满足固体火箭发动机复合材料壳体的结构功能一体化要求。      

TC4-DT材料高压电子束焊接框工艺研究

对TC4-DT材料高压电子束框工艺进行了研究。采用高压电子束焊接技术来实现复杂结构、大厚度难熔金属的热工艺成形,并对工艺、微观形貌、力学性能及微观组织进行系统性的分析。试验结果表明:电子束所形成的焊缝较为平整,成形较窄,拉伸、冲击强度较高,抗拉性能强于母材,但冲击韧性有所下降;焊缝接头网篮组织结构中,焊缝组织不见明显晶界,保证了焊缝组织的连续,且晶粒交错细化。     

Effect of beam current on microstructures and mechanical properties of joints of TZM/30CrMnSiA by electron beam welding

Electron beam welding experiments of TZM alloy and 30CrMnSiA steel butt joints were carried out with different beam currents. Microstructures and chemical compositions of typical zones were analyzed by optical microscopy, scanning electron microscopy and X-ray diffraction. The mechanical properties of the joints were evaluated by tensile strength tests. Besides, nanoindentation tests were carried out to compare the brittleness of the reaction layer and other typical microstructures. The results illustrated that the reaction layer at the interface between fusion zone (FZ) and TZM alloy was the weak position of the joint, which was divided into Fe₂Mo layer and a mixture layer of Fe₂Mo and α-Fe phases. As the beam current increased, the thickness of the Fe₂Mo layer decreased, which resulted in the increasing of the tensile strength of the joints. When the beam current exceeded 24 mA, the formation of the joint was poor with a low tensile strength. When the beam current was 24 mA, the joint presented the highest strength of 191.3 MPa and the joint fractured along the Fe₂Mo layer near the TZM alloy side with a brittle fracture mode.     

聚全氟乙丙烯塑料和金属连接试验研究

研究了热塑性氟塑料——聚全氟乙丙烯(FEP)和金属的连接方法，包括过渡层粘接和机械连接两种。采用自制的过渡层，利用模塑方法使FEP和不锈钢的粘接强度达到16MPa以上。同时采用机械滚边收口方法，可以提高FEP和金属含架的连接可靠性。     

铺放参数对复合材料厚度方向力学行为影响

为了探究铺放工艺参数的变化对复合材料厚度方向力学行为的影响,通过面外拉伸实验分析了铺放压力与铺放温度对复合材料厚度方向面外拉伸强度与拉伸模量的影响,并对不同铺放工艺的试件失效模式进行了分析。试验结果表明,增大铺放压力会减小层间富树脂区厚度,使复合材料面外拉伸强度不断增大,当铺放压力为0.225 MPa时取得实验组最大值,与铺放压力0.075 MPa相较强度提升约13.1%,失效模式由纤维断裂与纤维层剥离的组合转变为纤维断裂;铺放压力的进一步增大会挤压层间树脂,改变树脂富集形态,使面外拉伸强度下降,剥离失效模式再度出现。实验用复合材料的适宜铺放温度为30℃,过高的铺放温度会导致孔隙率的上升,使复合材料的面外拉伸强度严重下降,裂纹扩展失去规律性;与铺放温度25℃相比,铺放温度为45℃时复合材料面外拉伸强度下降达19.2%,失效模式由纤维断裂与纤维层剥离的组合失效转化为单一的纤维层剥离失效。     

Tensile properties analysis of CFRP-titanium plate multi-bolt hybrid joints

Hybrid joints have better tensile properties than pure bonded and bolted bolts, and are increasingly used in the aerospace field. Tensile tests are carried out for the Hybrid Bonded/Bolted(HBB) joints of Carbon Fiber Reinforced Polymer(CFRP) laminate and titanium alloy plate under different bolt numbers, and the corresponding load–displacement curves are obtained. At the same time, based on Continuum Damage Mechanics(CDM) theory, which is derived from 3D Hashin failure criteria, and a Cohesive Z...     

钛合金与不锈钢扩散焊中间金属的选择

采用铜和铜加钒作中间金属，探索了钛合金ＴＣ４与不锈钢１Ｃｒ１８Ｎｉ９Ｔｉ的真空扩散焊工艺，对接头成分、组织进行了分析。结果表明：采用一层中间金属铜进行扩散焊时，接头的强度很低，呈脆性断裂；采用两层中间金属铜加钒时，接头的强度与铜层的相对厚度有关，最高强度可接近母材不锈钢强度的下限。     

微量碳对阻燃钛合金焊接接头性能的影响

研究阻燃钛合金Ti-25V-15Cr,Ti-25V-15Cr-XC的电子束焊接头性能,对比分析母材中微量碳(C)对焊接接头性能的影响.试验结果表明,母材中的微量碳促使焊缝中形成较多的碳化物,提高接头的抗拉强度,降低接头的塑性,特别是大幅度降低焊缝的冲击韧性,仅为同状态不含碳母材焊缝的10%.     

基于红外热成像的TC4钛合金光纤激光焊接接头拉伸力学性能研究

对光纤激光焊接2.5mm厚TC4对接接头的拉伸力学性能进行研究,其研究方法为在常规的拉伸试验中,附加同步的红外热像测量,实时记录拉伸全过程中试样在力作用下温度场的变化。常规测试结果表明:接头与母材的强度相当,延伸率只达到母材的59.53%。试样温度场测试结果表明:当接头和母材受到的轴向载荷低于屈服强度对应载荷时,接头在热影响区部位会产生较大的应力集中,但接头和母材均未产生明显的塑性变形;当载荷等于屈服强度对应载荷时,均在宏观屈服点之前发生了微观的塑性变形;当载荷等于抗拉强度对应载荷时,接头发生剧烈塑性变形区域的长度只达到母材的35%,且接头与母材发生剧烈塑性变形区域的长度随拉伸过程的进行逐渐增加。     

碳纳米管对环氧树脂力学性能的影响

用浇铸成型法制备了碳纳米管／环氧树脂复合材料，研究了其力学性能，并探讨了该材料的微观结构与性能之间的关系。结果表明，碳纳米管对环氧树脂具有明显增强增韧作用。在碳纳米管加入量为3.0％(质量分数)时，复合材料的综合性能较好，拉伸强度、拉伸模量及断裂伸长率较纯树脂分别提高了90％-100％、60％-70％、150％-200％。     

TC4-DT钛合金线性摩擦焊接头组织和力学性能分析

针对飞机用典型的TC4-DT钛合金线性摩擦焊接头,开展组织及接头的拉伸、冲击和低周疲劳等力学性能测试。结果表明:TC4-DT钛合金线性摩擦焊接头经过700℃+保温3h的热处理后,接头的室温和高温抗拉强度达到母材的97%以上,室温和低温冲击性能略高于母材,室温低周疲劳性能与母材相当,具有良好的综合力学性能。     

CF3052/5284RTM 复合材料湿热性能

通过对CF3052/5284RTM复合材料进行试验研究,测定其在不同湿热条件下的基本力学性能,分析湿热条件对基本力学性能的影响。结果表明:湿热环境对该复合材料力学性能的影响程度不一,其中湿度的作用较温度更加明显;该复合材料在高温湿态条件下保持了较高的拉伸和纵横剪切强度,具有综合力学性能好、耐湿热性能好等优点。     

纤维增强树脂基复合材料连接结构强度与失效分析

采用拉伸试验和有限元分析方法研究纤维增强树脂基复合材料螺栓连接与胶–螺混合连接结构的失效机理。通过拉伸–剪切试验分析其载荷–位移曲线,结合有限元仿真结果及断面微观结构变化分析其结构强度和失效机理。结果表明,螺栓连接结构孔周碳纤维丝束受到螺栓挤压力变形后传递给树脂基体。因此,呈现纤维屈曲变形,树脂基体由均匀分布状被断裂的纤维短束挤压变成团簇状,形成结构不均匀而出现薄弱区域。胶–螺混合连接结构呈现拉伸断裂式破坏,断口处碳纤维丝束在拉伸–剪切作用下从环氧树脂基体中拔出并损伤断裂,丝束方向杂乱排布。附着在碳纤维丝束周围的树脂基体从均匀分布状变为团聚状,连接结构在达到极限载荷之后出现拉伸断裂,呈现净截面破坏,并且在重新分配载荷之后板材之间的胶粘剂对纤维的破坏会起延滞作用。材料强度、螺栓强度、胶层强度及螺栓宽径比等因素均会成为影响连接结构失效破坏的因素。     

磁场辅助激光熔覆铝基金属玻璃覆层

为提高铝合金的表面性能,采用磁场辅助激光熔覆的方法在5083铝合金表面制备了Al-Ni-Y-Co-La五元金属玻璃熔覆层,并对其进行组织成分及性能分析。实验结果表明：熔覆层主要由非晶相、α-Al相以及Al₄NiY等金属间化合物组成,旋转磁场的搅拌作用使熔覆层非晶相含量由10.2%提高到30.7%,且能够有效抑制多道搭接和多层堆积过程中重熔区晶粒的生长,细化了熔覆层晶粒组织,降低了残余应力,提高了显微硬度及韧性,使其平均显微硬度从278 HV_0.1提高至335 HV_0.1,且波动较小,平均抗拉强度为303 MPa,为基体拉伸件的110.2%,平均伸长率为6.79%,为基体的33.1%。     

一种潜伏性无卤阻燃中温固化环氧树脂体系

选用双氰胺和UR500为固化体系,自制阻燃剂M,制备一种预浸料用潜伏性无卤阻燃中温固化环氧树脂体系。结果表明,该树脂体系室温下储存期超过30 d,固化后力学性能优良,拉伸性能可达66. 5MPa,弯曲强度可达133 MPa,冲击强度可达10. 7 kJ/m2,阻燃防火性能优异,氧指数高达33. 1%,垂直燃烧满足UL-V0级,且可离火自熄。扫描电镜和热分析的结果表明,该体系优异的阻燃性能主要源于其燃烧后所成碳层的隔热隔氧作用。     

TA16钛合金导管的自动钨极旋转氩弧焊

针对2种规格的TA16钛合金导管开展不加填充的自动钨极旋转氩弧焊工艺试验,确定最佳的焊接工艺参数,并对其焊接接头的质量和性能进行了分析.结果表明:采用自动氩弧焊工艺焊接TA16钛合金导管,能够获得良好的焊接接头;接头室温拉伸强度能达到母材的95%以上;随着温度的升高,TA16导管接头的拉伸强度逐渐下降.     

A356-T6/6061-T6异种铝合金搅拌摩擦焊的工艺研究

通过对6 mm厚的A356-T6/6061-T6异种铝合金的搅拌摩擦焊工艺试验研究,采用OM、SEM、万能拉伸试验机、显微硬度仪等分析了母材位置、焊接速度对接头组织和性能的影响。研究结果表明:当旋转速度为1 000 r/min、焊接速度为100~400 mm/min时,均可获得内部无明显缺陷、外观良好的异种铝合金接头;A356-T6铝合金置于前进侧时有利于材料的迁移,焊缝区组织由典型的焊核区、热机械影响区和热影响区特征组织组成,焊核区域晶粒由表层向底层逐渐细化;接头拉伸性能随焊接速度的增加而增大;焊接速度较低时,A356合金位于前进侧有利于获得强度更高的接头,而焊接速度较高时,6061位于前进侧有利于获得高性能接头,且接头的屈服强度和延伸率均较A356位于前进侧时高;无论A356还是6061置于前进侧,接头的断裂位置均位于A356侧热影响区,与母材放置位置无关,这与焊缝硬度最小值区位置相吻合。     

2219厚板铝合金TIG和MIG焊接接头组织与性能对比研究

对15mm厚2219-C10S铝合金分别进行钨极惰性气体保护焊（TIG）、熔化极惰性气体保护焊（MIG）对接试验,对接头焊缝成形、内部质量、组织形貌及力学拉伸性能进行对比分析。结果表明：TIG焊缝表面光亮洁净,鱼鳞纹美观,焊缝内部近无缺陷,MIG焊接头焊缝飞溅较多,焊缝表面较为粗糙,焊缝内部存在少数单个小气孔。TIG焊缝晶粒尺寸较为细小,分布均匀,MIG焊盖面的焊缝组织晶粒则比较粗大,分布不均,热影响区比TIG焊接头的晶粒更为粗大。两种接头的熔合区组织不均匀,晶粒大小不一。常温拉伸试验中,两种接头均沿熔合区断裂,TIG焊接头强度和塑性要优于MIG接头。