预腐蚀疲劳退化加速因子研究
Investigation of acceleration factor for pre-corrosion fatigue degradation:model and analysis
-
摘要: 考虑预腐蚀对材料疲劳性能的影响,以疲劳强度作为腐蚀量,给出了考虑预腐蚀疲劳退化的加速腐蚀因子的定义和表达式,并结合疲劳分析方法,以细节疲劳额定值(DFR)作为疲劳强度的衡量,给出了预腐蚀条件下的DFR确定方法,通过加速环境和实际服役环境下DFR随预腐蚀时间退化规律的对比分析,建立基于DFR的加速腐蚀因子,并进行参数估计,最后,给出了LY12CZ铝合金试件在典型环境下的加速腐蚀因子取值.Abstract: The acceleration corrosion factor(ACF) for accelerated corrosion test under service or natural exposed environment is the most important parameter in the accelerated corrosion test(ACT).The material property was degraded seriously in pre-corrosion environment,and the corrosion damage was characterized by fatigue strength.So,the acceleration factor was defined as the ratio of fatigue strength in different environments,and the expression was proposed in consideration of the degradation process of fatigue strength with corrosion time.To evaluate the fatigue property,the pre-corrosion fatigue life was assumed to follow the two-parameter Weibull distribution,the detail fatigue rating(DFR) method in pre-corrosion environment was proposed,and the relationship between the DFRand the corrosion time was expressed as an exponential function.The acceleration corrosion factor based on the DFRwas proposed by comparing the degradation process in accelerated corrosive environment and the natural exposed environment,and was proved to be a constant regardless of corrosion time.Finally,the typical ACFof LY12CZ Aluminum alloy specimen was calculated.
-
[1] 宋兆鸿.航空发动机可靠性与故障抑制工程[M].北京:北京航空航天大学出版社,2002. [2] Simpson D L,Brooks C L.Tailoring the structural integrity process to meet the challenges of aging aircraft[J].International Journal of Fatigue,1999,21:1-14. [3] 刘文珽,李玉海.飞机结构日历寿命体系评定技术[M].北京:航空工业出版社,2004. [4] 曹楚南.中国材料的自然环境腐蚀[M].北京:化学工业出版社,2005. [5] Wanhill R J H,Luccia J J De.An AGARD-coordinated corrosion fatigue cooperative testing programme (CFCTP)[R].AD-A113731,AGARD-R-695,1982. [6] 贺小帆,刘文珽.疲劳关键件加速腐蚀因子可靠性分析[J].航空学报,2005,26(3):315-319.HE Xiaofan,LIU Wenting.Reliability analysis of accelerated corrosion factor for fatigue critical components[J].Acta Aeronautics ET Astronautica Sinica,2005,26(2):184-189.(in Chinese) [7] 高镇同.疲劳应用统计学[M].北京:国防工业出版社,1986. [8] 傅祥炯.结构疲劳与断裂[M].西安:西北工业大学出版社,1995. [9] Whittaker I C,Besuner P M.A reliability analysis approach to fatigue life of aircraft structures[R].AD 853263,1969. [10] Whittaker I C.Development of titanium and steel fatigue variability model for application of reliability analysis approach to aircraft structures[R].AD-758219,1972. [11] 林富甲.结构可靠性[M].西安:西北工业大学出版社,1991. [12] 陈群志.腐蚀环境下飞机结构日历寿命技术体系研究[D].北京:北京航空航天大学,1999. -
点击查看大图
计量
- 文章访问数: 1507
- HTML浏览量: 3
- PDF量: 419
- 被引次数: 0
下载: